对免振混凝土理论及配比试验结果讨论.docVIP

对免振混凝土理论及配比试验结果讨论摘要传统的混凝土施工技术已不能适应日异发展的高、大、难、新结构的需要，尤其是混凝土的振捣工艺，本文通过对免振捣混凝土的研究，着重解决混凝土振捣问题，依靠自身的高流动性，就能达到足够的密实度，满足混凝土施工中所需的高流动性要求，同时满足粘聚性、保水性及强度要求，通过多次试验与理论研究确定免振混凝土组成材料。 关键词混凝土高流动性免振捣配合比优化设计试验研究 中图分类号：TU528.53文献标识码：A文章编号： Abstract: The traditional architectural construction technology for concrete can no long meet the ever-increasing demands for new advanced and difficult structure, especially the concrete vibration density technology of concrete. This paper through the study of self-flowing concrete focuses on the solution of the problem of concrete vibration density. It proposes a method of relying on high-liquidity to achieve an adequate solidness to satisfy the demand high-liquidity demand of concrete construction process. As well as bond collect, keep water and strength. It composes lucid of self-flowing concrete material after a series of tests and theoretical studies. Key words: concrete high-liquidity self-flowingmix proportion optimum design test research 引言 人类社会的不断发展，使建筑艺术和技术得到高度的统一，建筑物外形体态各异，从而对现场施工也提出了更高的要求。以前建筑结构致密是依靠树木捣实的，随着科学技术的不继发展和进步，虽然现在在振捣方面有各种各样的工具可使砼密实，但还没有从根本上摆脱借助外物致密，只是从工具形式上发生了点改变。所以现在急需一种能节省材料和劳力就能使混凝土在自重作用下密实的方法，同时它的性能也不亚于用普通混凝土作业致密的程度。 本课题研究小组认为，所谓免振混凝土（Self-Flowing Concrete），是指混凝土拌合物不需振捣或者只需微微振捣就能达到普通混凝土各项性能指标的要求，同时具有高流动性、良好的体积稳定性和耐久性能、并具备加快施工进度、降低工程成本，节约工程造价的优势。 以上矛盾是不可调和的，所以减少和消除这些矛盾，改善混凝土结构，关键一条措施是掺入高效减水剂。本研究工作将采用加入高效减水剂+普通混凝土组成材料+外掺活性材料这一路线进行。 现阶段研究免振混凝土的必要性 现今的混凝土结构工程，不断向大规模、高难度、高层化方面发展，混凝土结构中的配筋也越来越密、越来越复杂，施工难度逐渐增大。与此同时施工噪音问题也变得尤其突出。因此需要一种既不需要振捣就能在重力作用下穿越稠密钢筋间隙又能填充复杂模型各个角落且能达到规定强度和耐久性、经济性、适用性等要求的混凝土。 据笔者观察，几乎所有的混凝土结构采用振捣法致密，采用振捣法虽可通过振动致密，但在振动过程中的絮动使骨料按比重不均匀沉降形成粗细骨料的分离，特别是采用泵送的高、深、大的剪力墙结构，由于拌合物入模时要落入2~3m高的模具，已经形成初步分离，如再经捣棒强力振动，势必加剧离析程度，所以研究免振捣的混凝土就有必要了。 研究依据与技术原理 根据经济适用原则，以控制混凝土的强度和拌合物的流动度为基准，进行拌合物的试配，从而确定选定原材料的配比材料用量。 １）用几种外加剂和几种水泥（本研究只选取了二种），对其进行组合制成水泥净浆，测定在某一特定材料下时的最大流动度和减水率； ２）根据自密实的要求，确定混凝土中砂、石含量占有率与堵塞的关系，从而确定粗细集料所占拌合物的质量比； ３）由于自密实混凝土拌合物所用胶凝材料量往往很大，同时易产生泌水离析，有必要用掺合料代替部分水泥来减小