喂丝法生产耐低温冲击球墨铸铁的应用.docVIP

喂丝法生产耐低温球墨铸铁的应用 王小伟，朱浩宇，张胜，黄伟，殷作虎 无锡永新特种金属有限公司 摘要：本文简述了风电类耐低温球墨铸铁件的需求势头。从芯线、喂丝设备和处理站等三个方面对喂丝法生产耐低温冲击球铁生产工艺及其关键技术作了全面阐述。探讨了喂丝法处理耐低温冲击球铁的优点。说明这种球化处理法是一种值得推广的球化处理新工艺。 关键词：喂丝法，球墨铸铁，低温冲击，风电铸件 Abstract：The demands and application examples of low temperature resistant nodular iron casting used in wind power equipment were introduced. The cored-wire injection nodularizing process and its key techniques were described including : composition and preparation of cored-wire, cored-wire injection equipment and nodularizing treatment station. the advantages of injection nodularizing process and the points must be paid attentions when using this nodularizing process are discussed. It is pointed out that this nodularizing process is a new nodularizing process worth popularizing 。 近年来，国内生产具有耐低温冲击性能要求的球墨铸铁件的单位越来越多，产量越来越大，主要原因是风力发电产业的快速发展，截至2010年底，中国全年风力发电新增装机达1600万千瓦，累计装机容量达到4182.7万千瓦，首次超过美国，跃居世界第一 图一：1.5MW轮毂 图二：wikov箱体 表3 规格 Mg RE Si Ba Ca 粉铁比 线重 球化剂 CWT-1 25~30 2.0~3.5 38~44 适量 适量 1.3~1.6:1.0 370~410 孕育剂 Bs-1A —— —— 70~75 适量 适量 —— —— 图三：喂丝处理站 2、生产过程 按照配料加入各种炉料，通过12T中频感应电炉融化铁水。取光谱样品和碳硅分析样进行检验，并调整成分到表4的要求范围内。升温到1480℃~1520℃出铁，进行脱硫处理。脱硫处理结束后扒渣、测温，1400℃~1430℃加入浮硅孕育，将铁水运送到喂丝处理站加入事先设定好的丝线量进行喂丝球化处理。处理后扒渣，测温并记录并浇注，浇注过程采用随流孕育。球化丝的加入量设定在0.8%，孕育剂加入量0.9~1.1%，随流孕育剂加入量0.1~0.15%。 两种产品的主要处理过程一样，轮毂处理铁水12.2T，wikov箱体处理铁水7.5T。两种产品的成分及工艺做适当调整，以满足不同材质的要求。 表4 材料 C(%) Si(%) Mn(%) P S Mg RE 原铁水 3.5～3.8 0.8～1.1 ＜0.20 ＜0.035 ＜0.030 铸件 3.5～3.8 1.7～2.0 ＜0.20 ＜0.035 ＜0.015 0.03～0.045 0.01～0.02 3、检测结果 铸件的主要性能检测取样采用附铸试棒（两种产品附铸试棒大小均为），低温冲击任性的检测（轮毂为-40℃，wikov箱体为-20℃）采用“V”型缺口检测，数据记录见表5。铸件全部经无损探伤检测为合格。 表4 抗拉 强度 延伸率 低温冲击 球化 级别 基体 组织 球径 大小 -20℃ -40℃ 1.5轮毂 352 25% —— 11/14/12 2 铁素体 5~6 Wikov箱体 412 26% 16/18/16 —— 2 铁素体 5~6 金相组织如图： 轮毂 ×100 wikov箱体 ×100 此后又进行了多种产品以及后续产品的试制，都满足了材质要求。 4、分析及探讨 低温冲击韧性反映材料断裂时吸收的能量，也反映快速形变条件下，材料抵抗裂纹萌生、发展和断裂的能力。是一个材料的韧性指标，也就是说具有较高低温冲击韧性的球墨铸铁件在-20℃或-40℃时具有较高冲击韧性，脆——韧性能转变温度较低，能够较好的克服冷脆。 现在用球化剂生产低温冲击韧性要求的铸件