二水石膏（Two water gypsum）.docVIP

二水石膏（Two water gypsum） Two water gypsum To help edit the encyclopedia business card two, the molecular formula for gypsum is CaS04 2H2 0. It can be seen that its chemical structure is calcium sulfate crystals with two crystalline water. In different conditions of heating treatment, the structure of water easily out, become a variety of crystals of hemihydrate gypsum and anhydrous gypsum. Catalog Two brief introduction of water gypsum solubility Two application of gypsum Gypsum and two water gypsum Character Crystalline water stage structure Two gypsum formation Expand the brief introduction of two water gypsum solubility Two application of gypsum Gypsum and two water gypsum Character Crystalline water stage structure Two gypsum formation Expand the edition of the two gypsum plaster. When the temperature is heated at 65 degrees, two gypsum will begin to release the structural water, but the dehydration rate is slow. At about 107 DEG C and when the vapor pressure reaches 971mmHg, the dehydration rate is rapidly becoming faster. As the temperature continues to rise, dehydration is accelerated, and at l 70 - L90 DEG C, the two gypsum becomes dehydrated at a very rapid rate and becomes alpha hemihydrate or beta hemihydrate. When the temperature continues to rise to 220 and 320~360 degrees, hemihydrate continues to dehydrate and becomes alpha soluble anhydrite. But the anhydrous 100% paste produced at 220 DEG C is easier to absorb water in the air and become hemihydrate gypsum. The anhydrous gypsum which is changed during the period of 450 to 750 DEG C is an insoluble anhydrite. This anhydrite is what we usually call dead burning plaster; it is difficult to dissolve in water, hardly coagulate, and has no strength. At 800 degrees centigrade, anhydrous gypsum begins to decompose into CaO and SO2 plus O2, where the condensation is mainly due to the condensation of CaO rather than gypsum. This decomposition is more intense at 1050 degrees centigrade and ends at 1350. In the r