冷法新型淀粉粘合剂的制备 张晓京，张晓荣，贾德彪，孙赢慧 （北方民族大学 材料科学与工程学院 宁夏 银川 750021） 摘要:本文论述了新型淀粉粘合剂的合成方法，以硫酸铜代替传统用硫酸亚铁作催化剂，选用草酸作粘合剂脱色剂，采用冷法制备新型淀粉粘合剂。制备的产品为乳白色，扩大产品适用范围。当催化剂硫酸铜用量为0.12%时，以粘度和初粘力为评价指标，通过正交试验确定了淀粉粘合剂的最佳配方为：水77.9%，淀粉17.3%，双氧水0.28%,氢氧化钠1.3%，硼砂0.12%。单因素实验证明草酸添加量为2.9%时即可得到良好脱色效果。 关键词 淀粉粘合剂；硫酸铜；草酸；脱色剂 中图分类号：??? ?????文献标识码：A Preparation of New Type Starch Adhesive at Room Temperature ZHANG Xiao-jing, ZHANG Xiao-rong, JIA De-biao and SUN Ying-huei (College of Materials Science and Engineering, Northern University for Nationalities, Yinchuan 750021, China) Abstract: This paper discusses a synthesis method of new type of starch adhesive, with copper sulfate instead of the traditional way by using ferrous sulfate as catalyst, which choosing oxalic acid as adhesive decoloring agent, with cold method to prepare novel starch adhesive. The colour of the prepared product is milky white in order to expanding the range of product applications. When the catalyst copper sulfate content is 0.12%, the viscosity and the Starting adhesive forces are regarded as evaluation index, the optimum formula was found through orthogonal experiment. It contents: water 77.9% , starch 17.3% , H2O2 0.28%，NaOH 1.3% , and borax 0.12%. The experiments using single factor show that it can get satisfied decolorizing effect when adding amount of oxalic acid was 2.9%. Key words: starch adhesive; copper sulfate; oxalic acid; decolorizing agent 前 言 淀粉粘合剂是近年来我国包装行业普遍采用的一种粘合剂[1],具有强度高、重量轻、无腐蚀、无污染、防潮性好、粘接性强、涂膜坚韧以及生产设备简单、制作方便和涂布量小等特点,是取代沿用多年的泡花碱的优良粘合剂[2-4]。它被广泛应用于各种纸制包装箱、袋、管的生产,也可用于壁纸、商标的粘贴,还可用于纺织产品上浆、制鞋业及棉织物粘接等。淀粉粘合剂的制作方法和生产工艺有很多,目前主要有碱糊法、糊精法和氧化法等[5]。利用氧化法生产的产品粘度高。氧化法又分为一步法和两步法,一步法生产工艺简单,设备投资小。作为一步氧化法又分为室温和加热两种方法,室温法制备氧化淀粉粘合剂具有无需加热, 粘合剂流动性好, 粘结力强, 可长期保存, 设备简单, 无环境污染等优优点[6]。但一般要加入催化剂硫酸亚铁提高反应速度，产物呈深褐色，不适合应用于要求较高的场合。 本方法采用硫酸铜为催化剂,草酸作为脱色剂，制得最终产品为乳白色，扩大产品适用范围。 1．实验 1.1 实验原料与试剂 市售马铃薯淀粉;硫酸铜(化学纯)、双氧水(化学纯,浓度30 %(质量分数,后同) ) ；氢氧化钠(化学纯,配制成10%的水溶液) ;硼砂(化学纯)； 草酸(化学纯,配制成30%的水溶液)。 1.2 实验