Lubrication performance of the base stocks with fullerols polymer derivatives as water-based lubricant additive are studied with four ball tester and Inverted Research Metallurgical Microscope (IRMM). The conclusion is as follows: Firstly, Experiments indicated that the addition of the fullerols polymer derivatives in the base stock with 0.5% OPZ can raise the anti-wear performance and load-carrying capacity of the base stock greatly. The outcome varies with the content of the fullerols polymer derivatives. The excessive addition results in the poor lubrication performance. Secondly, the wear scan diameter(WSD) of addition of the fullerols polymer s don’t increase with time after 20-30 seconds. It is as result s of strong hydrophobic effect and hydrogen bond . Thirdly, the addition of the polymer without fullerols also shows the improvement of the lubrication performance. But compared with fullerols polymer derivatives, the effective improvement is little. It is due to the absence of hard fullerols core in which is very important during lubrication. Additionally,fullerols also shows good potential application in biology. The experimental results of bioactivity show that the effect of which free radicle s damage the film of red blood cell is obviously decreased. It is also observed that our products can restrain the influence o f free radicles on aging. And the biological activities of those materials are under research. Keyword: fullerols fullerols derivatives lubrication additive bioactivity Water-soluble polymer This work was supported by Nati