多壁碳纳米管增强的cu-sn合金的显微组织和干滑动磨损行为 microstructure and dry sliding wear behavior of cu-sn alloy reinforced with multiwalled carbon nanotubes.pdfVIP

Trans. Nonferrous Met. Soc. China 26(2016) 1755− 1764 Microstructure and dry sliding wear behavior of Cu−Sn alloy reinforced with multiwalled carbon nanotubes 1,2 3 4 5 6 H. M. MALLIKARJUNA , K. T. KASHYAP , P. G. KOPPAD , C. S. RAMESH , R. KESHAVAMURTHY 1. Advanced Composites Research Centre (ACRC), P E S Institute of Technology, Bangalore 560085, India; 2. Department of Mechanical Engineering, GEC, K. R. Pet 571426, Karnataka, India; 3. Department of Mechanical Engineering, Atria Institute of Technology, Bangalore 560024, India; 4. Research and Development, Rapsri Engineering Products Company Ltd., Harohalli 562112, India; 5. Department of Mechanical Engineering, Alliance College of Engineering and Design, Alliance University, Bangalore 562106, India; 6. Department of Mechanical Engineering, Dayananda Sagar College of Engineering, Bangalore 560078, India Received 26 July 2015; accepted 26 November 2015 Abstract: Multiwalled carbon nanotubes (MWCNTs) reinforced Cu−Sn alloy based nanocomposite was developed by powder metallurgy route. The mass fraction of CNTs was varied from 0 to 2% in a step of 0.5%. The developed nanocomposites were subjected to density, hardness, electrical conductivity, and friction and wear tests. The results reveal that the density of nanocomposite decreases with the increase of the mass fraction of CNTs. A significant improvement in the hardness is noticed in the nanocomposite with the addition of CNTs. The developed nanocomposi