真空吸塑工艺操作规程（Operating procedures for vacuum plastic suction process）.doc

真空吸塑工艺操作规程（Operating procedures for vacuum plastic suction process） Operating procedures for vacuum plastic suction process 6-22 I. preparation of MDF 1. check the plate surface clean, will blow away the surface of the MDF wood and fiber, keep no dust on the surface, too much dust and fibers will cause a pock marked phenomenon. 2., for the cutting of MDF, and its four sides polished, should use as little as possible sandpaper grinding. In the spraying process, MDF four not because the fiber is too rough to pay glue is not uniform, causing pitting phenomenon. For the finished products of higher appearance, the recommended fineness of the sand paper is more than 800 items. Two. Attention of composite film L. different composite films have different reaction to high temperature. If the material is changed, the operation condition should be evaluated before mass production. 2., as far as possible the use of low plasticizer content of composite film, because the plasticizer in the film for a long time storage and high temperature environment, it may free surface, thus affecting the bonding effect. 3. for rigid composite film: it is recommended to use relatively short blister time, as well as relatively high blister temperature. 4. for soft composite films: it is recommended to use relatively long blister time, and relatively low blister temperature. Three. Moisture content of MDF 1.. The moisture content of MDF should be controlled at 6% and 14%. 2. the optimum bonding condition requires the moisture content of MDF to be controlled at 8% 12%e Four. Storage and mixing of bonding and curing agents L. under normal circumstances, I vacuum plastic parts can be used in a single component to meet customer requirements. 2., if the customers heat resistance requirements of the product more than 70 degrees, or the production workshop temperature, humidity is too high, it is recommended to use curing agent. The dosage of curing agent is 3%, 5%. 3. the proportion of main agent and c