房屋建筑墙体开裂的原因及应对措施（Causes and Countermeasures of wall cracking in housing construction）.docVIP

房屋建筑墙体开裂的原因及应对措施（Causes and Countermeasures of wall cracking in housing construction） Causes and Countermeasures of wall cracking in housing construction [Abstract] according to the relevant statistics, due to cracking wall appearance and impact of housing security incidents accounted for most of the general, reticular crack and longitudinal crack crack problems, although some cracks and no serious threat to the safety of construction and appearance, but the cracks to rain water provides the leakage passage, while causing a falling plaster layer and all these problems in peoples normal life influence. This paper analyzes the causes of wall cracks in buildings, and based on this, probes into the usual technical measures for repairing wall cracks and the application of new building materials in the cracking of exterior wall of buildings. [Key words] wall cracks; causes; Countermeasures 0. Preface Since the reform and opening up, with the rapid development of Chinas economy, peoples living standard continues to improve, people pay more and more attention to the quality of residential construction, while improving the living environment at the same time, there are inconvenience that the current building wall crack is more common to have a direct impact on the wall the decorative effect, to a certain extent people. 1., housing construction wall cracking reasons 1.1 wall cracks caused by temperature stress Generally, materials have the property of thermal expansion and cold contraction, and the temperature deformation refers to the expansion and contraction of the house structure due to the change of ambient temperature. If the structure is restrained and can not be deformed freely, additional stress or thermal stress will be added to the structure. Once the structure is free of any constraints, it can deform freely when the temperature changes, so that additional stress does not form in the structure. The expansion value of the structure caused by temperature stress. At