硅灰对高强混凝土强度影响的试验研究 摘要： 在高强混凝土中掺入适量的硅灰，对提高混凝土的劈裂抗拉强度有非常明显的效果，也可在一定程度上增强混凝土的抗压强度和抗折强度。掺量低于或高于适量范围，对提高混凝土的强度作用很小。在实际工程混凝土中合理掺用硅灰，不仅可以提高混凝土的强度，而且变废为宝，改善环境，技术、经济和社会效益显著。 关键词： 高强混凝土；掺合料；硅灰；强度 中图分类号： TU528.041 文献标志码： A 文章编号： 1002-3550（2011）07-0074-03 Experimental research on the effect of silica fumtothestrength of high- strength concrete WANG Hong，CHENWei-tian，CHEN Chang-li（School of Materials and Architectural Engineering，Guizhou Normal UniversityGuiyang 550059，China） Abstract: It has obvious effect of mixing appropriate quantity of silica fume in high-strength concrete to enhance its splittintensile strength，and could increase its compressive strength and flexural strength to a certain extent.However，it could be useless for strength enhancing if the mixingquantity is lower or higher than the appropriate quantity.Reasonable mixing silica fume in engineering concrete not only increase the strengthbut also recycle waste material and improve environment and technique which has remarkable economic and social benefits. Key words: high-strength concrete；mineral admixture；silica fume；strength 硅灰（Silica Fume）又称硅粉，是在冶炼工业硅或含硅合金时由高纯度的石英与焦炭在高温电弧炉（2 000 ℃）中发生还原反应而产生的工业尘埃。它是利用收尘装置回收烟道排放的高温废气并通过专门处理而得，其颗粒超细，比表面积大，具有很高的火山灰活性。硅灰用于混凝土的研究始于20 世纪50 年代的挪威、丹麦等国，在美国、日本、法国等国得到了普遍的应用。 在我国，通常将硅灰作为掺合料用于混凝土工业中，一方面可节约水泥熟料，降低混凝土的生产成本，有效减少环境污染，保护环境；另一方面，改善混凝土的性能，延长结构的安全使用期，增加工程的使用寿命[1]。因此，开发硅粉在混凝土中的应用，对促进节能减排、废弃物的资源化利用和保护环境、发展循环经济，以及建设资源节约型、环境友好型社会具有重要的现实意义，其技术、经济、社会效益显著，应用前景广阔。 目前，硅灰已成为高强混凝土的重要组分。本研究通过试验，研究了硅灰对高强混凝土强度性能的影响，供工程技术人员参考。 1 试验 1.1 试验用原材料 （1）水泥：试验使用P·O 42.5 级水泥，其化学成分与物理力学性能见表1、2. 表1 水泥的化学成分% 化学成分 Na2O CaO SiO2 Al2O3 Fe2O3 MgO SO3 K2O Cl f-CaO Loss 含量 0.18 60.19 20.58 5.58 2.84 2.47 2.18 0.48 0.03 1.94 4.04 表2 水泥的物理力学性能 密度 /（g/cm3） 比表面积 /（m2/kg） 标准稠度用水量/% 初凝 终凝 安定性 抗折强 /MPa 3 d 抗折强 /MPa 28 d 抗压强度/MPa 3 d 抗压强度/MPa 28 d 3.06 355 27.5 179 238 合格 5.39 8.20 25.9 48.6 （2）硅灰：试验所用硅灰的化学成分和物理力学性能，见表3。 表3 硅灰的化学成分和物理力学性能 SiO2 Al2O3 Fe2