玻璃幕墙安全隐患和预防措施探究.docVIP

玻璃幕墙安全隐患和预防措施探究 　　摘要：随着我国城市的发展，一批批高层建筑拔地而起，一座座晶莹剔透的玻璃幕墙，浑厚庄严的石材幕墙和轻巧整洁的金属幕墙临街排布，形成了城市美丽的风景线，但这美丽的建筑也会成为杀手，从天而降的玻璃砸伤行人车辆的事情也常见报端。本文针对玻璃幕墙安全隐患进行分析，从而引起同行人士的警觉与重视，减少幕墙安全隐患。 Abstract： Along with the development of the cities in China， countless high-rise buildings springing up， the glittering and translucent curtain walls， vigorous majestic stone material curtain walls and light metal curtain wall range along the street， which form beautiful scenery line of the city， but the beautiful buildings will also be a killer， the incident of pedestrian and vehicle be injured by a glass dropping from the skies often are reported. This paper analyzed hidden safe dangers for glass curtain wall， so that it can cause the peer’s vigilance and attention to reduce the hidden safe trouble. 关键词： 玻璃幕墙；安全隐患；自爆；预防措施 Key words： glass curtain wall；safe dangers；spontaneous explosion；preventive measures 中图分类号：TU767 文献标识码：A 文章编号：1006-4311（2013）20-0101-02 玻璃幕墙是一种新型的墙体，装扮出美丽的建筑，又有着节能环保的优势，玻璃幕墙在建筑方面得到广泛应用，由玻璃高空坠落引发的安全问题也逐渐增多，常见的玻璃坠落原因有玻璃自爆和玻璃脱落引起。 钢化玻璃在没有外部直接作用的情况下自动发生破碎的现象即为钢化玻璃自爆。按照导致钢化玻璃自爆的原因可以分为以下两种[1]：第一，由于玻璃的沙粒、缺口、气泡以爆边等可见缺陷导致的自爆；第二，玻璃中硫化镍（NiS）杂质膨胀引起的自爆。由于导致这两种自爆的类型不同，应当采用不同的处理方法进行对待。第一种检测比较容易，因此在生产中就可以控制。而第二种无法目测检验故而不可控。因此，安装前剔除第一种，而第二种则继续存在，成为导致自爆的主要因素。 玻璃自身的质量对与自爆的影响也很大。由于平板玻璃相对浮法玻璃而言均匀度和平整度交叉，因此其承受风荷载以及热应力能力也比较弱。为了提高其热应力以及抗风压能力可以对玻璃进行半钢化和钢化。由于钢化玻璃承受的抗压强度和抗张强度比普通玻璃高很多，所以能够经受弯曲以及温度变化，从而减少了玻璃的自爆几率。 除了玻璃自身质量外，玻璃的几何形状、安装后四周的紧固程度、玻璃与四周铝合金的密封以及后续工艺的受热状况等都能影响玻璃的自爆概率。玻璃本体部位的不均匀也会导致玻璃的热应力自爆，上墙后的玻璃由于受到阳光的照射将光转化为热能，从而形成玻璃四周的热膨胀。如果镶嵌在铝合金框内部由于部分受不到阳光照射而导致受热不均匀从而形成热应力，当张应力大于玻璃的抗张强度时就会导致玻璃破裂。夏季下雨时由于雨水降温，使得玻璃内外表面温差急剧加大，内应力随之加大，导致玻璃爆裂，所以雨后是玻璃自爆的几率较大。玻璃自爆由于不可避免性和随机性，形成了玻璃幕墙的最大安全隐患，怎么预防和减少玻璃自爆的危害性呢，主要从减少自爆，和减少自爆危害性两方面。 设计方面，因为平板玻璃自身质量缺陷，目前已经不用或少用平板玻璃。由于钢化玻璃生产过程不可避免的产生硫化镍杂质的存在，自爆风险一直存在，选用半钢化玻璃就避免了玻璃幕墙自爆的风险，因为半钢化玻璃表面应力较小，就不存玻璃自爆的问题。一定要通过计算选择玻璃的厚度，同一个面积的低层和高层的受力差别很大。玻璃的厚度、面积由于玻璃使用的高低和地区不同，应当根据计算予以调整。 加工方面，钢化玻璃制作时热浸等工艺处理，释放玻璃表面应力，可以减少玻璃的自爆，玻璃边缘处理也能减少玻璃的自爆。 为了减少玻璃受热膨胀导致的自爆，在安装玻璃时在下