低温压力容器用钢的现状与发展概况-中国变压吸附设备商务网.PDFVIP

　技　术　综　述　 低温压力容器用钢的现状与发展概况 张 　勇 (安徽省特种设备检测院 ,安徽 合肥 　230000) 摘 　要 :简要介绍了 C - Mn ,调质高强度和Ni 系低温压力容器用钢的现状、分析了各国及各企业相 应产品之间主要技术指标的差异 , 明确了中国在 0. 5Ni 等低温压力容器用钢方面已处于国际领先 水平 ,概述了各类低温压力容器用钢的发展动向。 关键词 :低温 ;压力容器 ;钢材 ( ) 中图分类号:TB35 ;TH49 　　文献标识码 :B 　　文章编号 :1001 - 4837 2006 04 - 0031 - 04 Current Situation and Development of Steels Used for Low Temperature Pressure Vessel ZHANG Yong (Anhui Special Equipment Inspection Institute ,Hefei 230000 ,China) Abstract :This article briefly introduced C - Mn steels , the quenched and tempered high strength steels and Ni steels used for the low temperature pressure vessel. And the main technical conditions difference between the various countries and various enterprises corresponding product was analyzed. It was clear that China has been in the international leading level in the 05Ni steel used for the low temperature pressure vessel. The develop ment trend of steels used for the low temperature pressure vessel was summarized. Key words :low temperature ;pressure vessel ;steels 　　随着石化工业的发展 ,新工艺、新设备不断出 196 ℃含 55 %～9 %Ni 钢) [3 ,4 ] 。可见 , 随着 Ni 含 现 ,气体的液化、分离、贮运及应用在各国已很普遍 , 量的增加 ,使用的温度可更低。 这些低温技术和设备的开发促进了低温压力容器用 但是 ,Ni 元素的价格较高 , 同时钢中Ni 含量的 [1～4 ] ( 钢的发展 。 增加 ,也使得钢材的某些性能 如焊接性、表面质量 ) 各国定义低温压力容器的温度基本是 0～ - 20 等 变差。因此 , 随着冶炼、轧制和热处理等工艺及