以Span80与Tween60为混合表面活性剂微乳液探究.docVIP

以Span80与Tween60为混合表面活性剂微乳液探究 　　摘要：本文研究了Span80和Tween60为混和表面活性剂的微乳液的形成，分别采用滴定法和电导率法，考察了Span80和Tween60复合表面活性剂在体系中质量比、Span80和Tween60的复配比、助剂的加入量、油相种类、温度等因素对微乳液最大增溶水量的影响，探明了该体系形成微乳液的较适宜的条件。 关键词：微乳液；Span80；Tween60；电导率Abstract:The formation of Span80 were studied in this paper and the Tween60 microemulsion mixed surfactant, respectively by titration method and conductivity method, the effects of Span80 and Tween60 composite surface active agent in the system mass ratio, Span80 and Tween60 mixed ratio, additive quantity, oil phase, temperature and other factors on the microemulsion the maximum solubilization effect, the suitable conditions of the system proved the formation of microemulsion. Keywords: Span80; Tween60; microemulsion; conductivity 中图分类号：TQ423 文献标识码：A文章编号： 1 试验原理及方式 W/O型微乳液的最大增溶水量是此类型微乳液在相应条件下稳定存在的极限条件，加入水量超过最大增溶水量以下的区域是此条件下微乳液稳定存在区域，因而需寻求最大增溶水量的适宜条件。 称取不同量的Span80和Tween60，得到不同的HLB值的表面活性剂。混合表面活性剂的HLB值，按下式计算： HLB = HLBS * Ws + HLBT * WT 式中：HLB为span-tween复合表面活性剂的亲水亲油平衡值； HLBS，HLBT分别为span，tween的亲水亲油平衡值； Ws，WT为Span80和Tween60的质量分数。 用original lab绘图软件对测量得到的电导率作图，通过曲线的突变点来确定微乳液的最大增水量。比较不同HLB值对最大增溶水量的影响。 可以通过对体系的电导率变化测试了解其最大增溶水量值。也就是判定以Span80和Tween60为表面活性剂所形成的W/O型微乳液体系中Span80和Tween60为微乳液复合表面活性剂的最佳配比。进而研究Span80和Tween60的主要性质为本次研究的主要目的。得到一个比较具体的数据与更详细的本复合表面活性剂的使用范围，给使用到本复合表面活性剂提供一个最佳的使用环境与条件。 2 实验结果与讨论 2.1Span80和Tween60复合表面活性剂在体系中所占最佳质量比 在试验的过程中，开始时导电率随着加水量的增多呈下降趋势；当水量加到一定量时，电导率会逐渐上升。当非离子表面活性剂溶于油相中时，所得乳液的电导率（0.150～0.250μs/cm）比纯油相的高。随着加水量的增大，加入的水和更多的亲水基（极性基团）被禁锢起来使其不能导电，从而乳液的导电率下降。当水量增大到一定值时，一方面没有更多的表面活性剂的亲水基将水分子包裹起来；同时被包裹的水核逐渐增大，并开始向双连续相转变，慢慢由油包水变为双连续相。此时电导率会随着加水量的增加而逐渐增大。随着加水量的进一步增多液体开始慢慢由双连续相向水包油型转变。当微乳液由油包水向双连续相转变时电导率必然有一个增大的转变，此突变点对应的加水量即为油包水型微乳液的最大增溶水量。因此通过对电导率的全程观察可以更加灵敏的找到此体系所可以接受的最大增溶水量，并且更加准确。 图1表面活性剂所占质量分数与最大增溶水量的变化曲线 表1活性剂所占质量分数为14%溶水过程中电导率的变化 试验数据表明Span80和Tween60为复合表面活性剂在油相中的使用最佳所占质量分数为14％，太低能够形成微乳液的环境会更苛刻，太高则会使体系变膏状凝固态。 2.2Span80和Tween60最佳复配比. 在25℃下，固定体系总质量20g，Span80和Tween60所占质量分数为14％时（油相＝17.2g）醇量1.