1铝轧制工艺的第一部分.docVIP

1. Rolling process of aluminum　 铝轧制工艺 1.1 Overview　　　 概况1.1.1 Current situation of rolling process 轧制工艺的当前形式 　　　　　　　  　Shipment amount of domestic aluminum products expresses, as shown in Fig. 1.1.1, a trend of some decrease for these several years by effect of downturn in the economy, however, the past 10 years shows approximately double increase. Among them, can stock shows the biggest share and increase of its production quantity is remarkable. To comply with this growth in demand, each domestic company has promoted enhancement of rolling mills as shown in Table 1.1.1. Trend of main equipment enhancement in foreign countries is also shown in Table 1.1.1, and new installation rush of rolling mills in USA of 1980s is remarkable. 国内铝产品消费的发货数量如图1.1.1所示，受经济萧条形式的影响，这几年有一些下降的趋势，但是在过去的10年里，大约翻了一番。其中，罐料生产数量的增长十分显著，体现了最大的份额。为了满足市场需求增长的需要，每个国内的公司已经进行了轧机的扩建，如表1.1.1所示。表1.1.1中也显示了外国的主要设备扩建的趋势，在80年代美国轧机的新安装潮流十分显著。 图1.1.1 Transition of shipment amount of domestic aluminum products ( Search by Japan Aluminum Association) 国内铝产品装运数量变化情况（日本铝业协会研究提供）  Table 1.1.1 Recent trend of enhancement of aluminum rolling mill (after 1981) 表1.1.1 近年来铝轧机增加的趋势(在1981年以后) 完成 公司 工厂 热轧机 冷轧机 1981 Kobe Steel神钢 Mooka (日本) 新建 2240 mm 1650 m/min 1983 Furukawa Al古河 Fukui (日本) 新建 R 4320 mm 新建 2750 mm 新建 工厂 ( Furukawa Denko at present现在的古河Denko ) F3－T 2850 mm Reynolds雷诺兹 McCook (美国) 新建 2240 mm Conalco Hannibal (美国) 新建 1984 Kaiser 恺撒 Trentwood (美国) 更新 F.5－T W.M. 1730 mm Fully cont. 1986 Alcan加铝 Logan City (美国) 新建 新建 新建 工厂 Pechiney匹兹涅（普基） Rhenalu (法国) 新建 1850 mm 1800 m/min 1987 Alcoa美铝 Warrick (美国) W.M. 2060 mm Alcoa美铝 Tennessee (美国) 新建 2030 mm Fully cont. 1988 Furukawa Al古河 Fukui (日本) 新建 1760 mm 1800 m/min Kobe steel神钢 Mooka (日本) 更新 F.3-T→F.4-T 1990 SKY Al Fukaya (日本) 新建 2240 mm 1800 m/min 1991 Sumitomo Light Metal住友轻金属 Nagoya名古屋 (日本) 新建 2240 mm 2000 m/min 1992 Mitsubishi Al三菱铝 Fuji (日本) 新建 1930 mm 1000 m/min Sumitomo Lig