毕业设计（论文）-低碳钢表面渗硼工艺的研究.docVIP

郑州大学毕业设计（论文） 题　目：Study on the processing of the surface boroniding of the low carbon steel 学生姓名 指导教师 班 级 材料成型与控制工程06级 专 业 材料成型及控制工程 学 院 材料科学与工程学院 2010年6月2日摘要 ABSTRACT This paper is about the research on the surface boroniding process of the low carbon steel. There are three variables used in this experiment；the ratio of the borax、holding time and temperature of boroniding. Three different experiments were done about each variable。By the comparison of the appearances of sample after boroniding in the different ratio of the borax，It is found the ratio of the borax was very important . If the borax was used too much，it was easy to cause the serious agglomeration . By the comparison of the microstructure of the samples after boroniding with the different holding time，it is found that the best holding time was five hours. By the comparison of the microstructure of the samples after boroniding at the different holding temperature，we knew that as the increasing of the temperature，the thickness of the boride layer also increased within certain limits.And the proper temperature is about 920℃. At the end of the article，the best processing technique was made. Key words: the low carbon steel, boroniding , processing. 目 录 要 ii ABSTRACT iii 1概述 1 1.1 绪论 1 1.2低碳钢介绍 1 1.2.1低碳钢的特点 1 1.2.2 低碳钢的应用 1 1.3表面渗硼 2 1.3.1 表面热处理介绍 2 1.3.2渗硼 2 1.3.3渗硼方法 3 1.4渗硼的应用 3 1.4.1冷作模具渗硼 3 1.4.2 热作模具渗硼 3 1.4.3渗硼技术的其他应用 4 1.5选题意义 4 1.6实验中需解决的问题 4 2 实验过程 5 2.1渗硼工艺 5 2.1.1母材的选取 5 2.1.2渗硼配比及处理工艺的制定 5 2.1.3渗硼前准备 6 2.1.4进行渗硼 6 2.2 试样的制备 6 2.2.1试样的截取 6 2.2.2制作金相试样 7 2.3金相观察 8 2.4显微硬度的测量 8 3 实验结果分析 9 3.1渗层组织形貌分析和硬度 9 3.2 过渡层组织分析和硬度 10 3.3 基体的组织分析和硬度特点 11 3.4 渗剂中硼砂含量的影响分析 12 3.5 保温时间的影响 13 3.6 温度的影响 13 3.7 现场 14 4 结论 15 参考文献 16 附件1：毕业设计（论文）任务书 17 附件2：郑州大学毕业论文开题报告表 18 附件3：毕业设计（论文）计划进程表 20 附件4：郑州大学毕业设计中期检查表 21 附件5：毕业设计（论文）成绩评定表 22 外文翻译 23 翻译原文 32 致 谢 37 1概述 1.1 绪论 渗硼工艺自诞生至今已有100多年的历史，此间国内外的同行们创造发明了许多渗硼方法，如固体粉末渗硼、气体渗硼、膏剂渗硼、盐浴渗硼等，其中固体渗硼因具有操作方便、使用设备简单、质量易控制等优