维普资讯 第 53卷 第 10期 化 工 学 报 VOT．53 № 10 2002年 10月 Journal of Chemical Industry and Engineering (China) October 2o02 水解聚丙烯酰胺盐水溶液半经验流变方程 杨菊萍 (浙江工程学院应用化学系，浙江 杭州 310033) 关键词 水解聚丙烯酰胺 零切黏度 表观黏度 流变曲线 中图分类号 0 63 文献标识码 A 文章编号 0438—1157 (2002)10—1089—03 SIM ULATIoN oF APPARENT VISCoSITY FoR HPAM SALT SOLUTIoN YANG Juping (Departmentof AppliiedChemistry，ZhejiangInstituteofScienceandTechnology，Hangzhou310033，Zihejiang，China) Abstract Two assumptions were putforward as a resultOf analysis Ofthe flow curves 0fhydrolyzed polyacrylamide—saltsolutionandthetheoryofmacromolecularoslution．Therelationshipsbetweenthezero— shearviscosity r／0na dpolymerconcentrationslDp，between theocnstnatsK and in Meter’Sequation and polmy erocncentrationPpwereestablished．ThereforeauniversalMeter’Sequationrelatingappraentvisocsityr／a withpo lmy erocncentrationlDpwasdeduced．Theqeuationcanbeusedtosimulateappraentviscosity aforthe system ．withna averageerrorof7．9％ ofrexperimentalvalues ． Keywords hydrolyezdpo lyacrylamide，ezro—shearviscosity，appraentviscosity，rhelogicalcurve 引 言 非 匠 稚 (1) 聚合物驱油数值模拟黏度可减少大量的测试工 式中 k为幂律式指前常数 ， 为流变行为指数． 作 ，在驱油过程中有十分重要的地位．但是 ，目前 由于 HPAM 是聚电解质 ，其盐水溶液的流变行为 这方面研究报道还很少．本文的研究 目的是通过幂 与其结构形态密切相关．根据高分子溶液的缠结理 律方程…1和高分子稀溶液理论 [2-5]建立一个表观黏 论_7J，对于同一盐浓度 (c)、同一温度下的HPAM 度半经验流变方程 ，为聚合物驱油过程黏度预测提 溶液 ，当 7．／很小时，聚合物浓度 (』D。)越大 ，则分 供可靠的依据． 子链缠结越严重，内摩擦阻力越大 ，刁0越大 ；当 水解聚