水泥基大掺量粉煤灰、氟石膏干粉抹面砂浆的研制 Development of Cement-based Dry-powder front Mortar with Large Content of Fly Ash and Fluorogypsum.pdfVIP

粉煤灰综合利用 FLYASH COMPREHENSIVEUTII。IZATl0N 2008NO．1 水泥基大掺量粉煤灰、氟石膏干粉抹面砂浆的研制★ ofCement-basedfrontMortarwith Contentof Ashand Development Dry-powder Large Fly Fluorogypsum 周万良，詹炳根，龙清华 (合肥工业大学土建学院路桥系，合肥市230009) 摘要：用水泥、粉煤灰和氟石膏配制的胶凝材料(CBFF)，干粉抹面砂浆具有体积安定性好、水硬性和干缩小的特 点。随甲基纤维素醚掺量的增加。该砂浆的沉入量先增加后减小，保水性不断变好。在该砂浆中单独加入木质纤维素， 随掺量的增加，砂浆和易性不受影响．但砂浆的强度缓慢减小。 关键词：水泥基；大用量；粉煤灰≠氟石膏；干粉抹面砂浆 中图分类号：TU432+．5文献标识码：A 文章编号：1005—8249(2008)01—0007--05 (SchoolofCivilandArchitectural of 230009) Engineering。HefeiUniversityTechnology，Hefei this binder(CBFFbinder)waswith ashand bind— Abstract：Inpaper，the preparedcement，flyfluorogypsum．CBFF erischaracteristicof material，andlow theincreaseofthe volume goodsoundness，hydraulicdryshrinkage．With blending of ofCBFFmortarincreasesandthendecreases，butits becomes methylcetlulose，thesinkage water．containingcapacity moreandmore theincreaseofthe volumeof addedintoCBFFmortar．the good．With blending lignocellulosesingly ofCBFFmortar theits decreases． workability keepsunchanged，butstrengthslowly frontmortar Keywords：cement—based；largecontent；flyash；fluorogypsum；dry-powder 干粉砂浆也叫干拌砂浆、干混砂浆，是指在专门的 者复合起来也不能成为胶凝材料，因为氟石膏对粉煤 生产厂家内，将胶凝材料、细集料、外加剂和填充料等 灰的激发作用要在粉煤灰被碱性激发剂激发后才能发 按一定比例混合而成的干粉状材料。干粉砂浆用袋装 生。但如果将水泥和粉煤灰、氟石膏复合在一起，则能 或散装的形式运到建筑工地后，按一定的比例加水后 形成胶凝材料，因为水泥作粉煤灰的碱性激发剂，氟石 就可直接使用。与现场拌制的砂浆相比，干粉砂浆具 膏作粉煤灰的硫酸盐激发剂，使粉煤灰的活性得到充 有质量好、生产效率高、品种丰富和环境友好等特点。 分激发，这样既可以使粉煤灰和氟石膏得到有效利用， 在欧美一些