See discussions, stats, and author profiles for this publication at: /publication/257766098 Synthesis and properties of dental zirconia–leucite composites Article in ulletin of Materials Science · December 2010 DOI: 10.1007/s12034-011-0136-y CITATIONS READS 2 33 7 authors, including: Xing Yin Stanford University 13 PU LICATIONS 130 CITATIONS SEE PROFILE Some of the authors of this publication are also working on these related projects: Wnt Signaling and Its Contribution to Craniofacial Tissue Homeostasis View project Rescuing failed oral implants via Wnt activation View project All content following this page was uploaded by Xing Yin on 28 May 2016. The user has requested enhancement of the downloaded file. 第27 卷 　第4 期 材 　料 　科 　学 　与 　工 　程 　学 　报 总第120期 Vol 2 7 　No 4 J our nal of Mat erial s Science Engineerin g A ug . 2009 文章编号 (2009) 氧化锆/ 白榴石复合烤瓷材料的性能 1 ,2 2 2 3 1 1 康 　明 ,尹光福 ,廖晓明 ,尹 　星 ,孙 　蓉 ,刘 　军 (1. 西南科技大学材料科学与工程学院 ,四川 绵阳　621010 ; 2 . 四川大学材料科学与工程学院 ,四川 成都 　610065 ; 3 . 四川大学华西口腔医学院 ,四川 成都 　610041) 　　【摘 　要】　以钾长石 、碳酸钾和氧化锆为主要原料 ,通过高温固相法一次性合成氧化锆/ 白榴石复合烤瓷材 料 。利用电子万能试验机测试样品的力学性能 ,利用 SEM 、XRD 、Raman 、EDX 和热膨胀仪测试样品的形貌 、物相 、 组成和热膨胀系数 。结果表明 ,样品的弯曲强度为 110M Pa 、断裂韧性为 3 . 5M Pa/ m1/ 2 、金瓷结合强度为 45M Pa ;在 样品中同时存在白榴石和氧化锆两种晶相 ,这既有利于增强烤瓷材料的力学性能 ,又有助于调节烤瓷材料的膨胀 ( - 6 ) 系数 约为 13 . 73 ×10 / K ,使其与牙用镍铬合金相匹配