水溶型丙烯酸酯印花台板胶的研制研究.pdfVIP

H025 水溶型丙烯酸酯印花台板胶的研制 李璐 文秀芳 皮丕辉 程江 杨卓如 （华南理工大学化工研究所，广东广州 510640 ） 摘 要 研究了水溶型丙烯酸酯印花台板胶的合成和单体的滴加方式，讨论了交联单体的用量、 软单体的种类、增稠剂的添加方式和用量、助溶剂和水的比例等对台板胶性能的影响，研究结果 表明，使用 13g 交联单体和其余单体分开滴加，以丙烯酸丁酯作为主要软单体，0.25g 聚乙烯醇 增稠剂在反应前加入，助溶剂与水的比例为 2 ：1，合成得到的台板胶性能优异。 关键词 水溶型 丙烯酸酯 台板胶 印花 SYNTHESIS STUDY ON THE WATER-BONE ACRYLATE TABLE ADHESIVE LI Lu WEN Xiufang PI Pihui CHENG Jiang and Yang Zhuoru (Research Inst. of Chemical Eng., South China Univ. of Tech) Abstract In this study, the synthesis of the water-bone acrylate table adhesive and the way of the monomers added to were investigated. The influence of the cross －linking agent, the thickener, the radio of the lacquer solvent/water and monomer type were discussed. It was found that 13g cross －linking agent was added separate from other monomers, butyl acrylate (BA) as main soft monomer better than 2-ethylhexyl acrylate (2-EHA), 0.25g thickeners were added before the reactor beginning,, lacquer solvent/water ratio was 2/1, and hence obtain a table adhesive with good performance. Keywords water-bone table adhesive acrylate calico printing 前言 在纺织物印花的过程中，为了保证印花的顺利进行和准确的套印精度，需要将柔软的纺 织物平整牢固地附着于印花台板上，常采用在印花台板上涂覆粘合剂的方法，要求这种粘合 剂能在瞬间将纺织物固定于台板上，持粘时间合适，以使印花结束后织物易于剥离，不会污 染纺织物，俗称这种粘合剂为台板胶。常见的台板胶有三类：淀粉类，腊酯类和合成树脂类， 其中合成树脂类由于具有高的粘合强度而逐渐成为台板胶发展的主流。丙烯酸类台板胶因为 原料价廉易得，生产设备简单，成本低等优点而得到了飞速的发展[1,2] 。 丙烯酸酯型印花台板胶有溶剂型，乳液型和热熔型等多种类型。溶剂型台板胶耐水性好， 粘性大，初始粘接强度高，但是其中使用了大量有机溶剂，会在操作中给生产者造成中毒的 危害。出于环保的考虑，迫切需要一种无污染的产品取而代之[3] 。本研究正是基于此点，发 1 展水溶型丙烯酸酯印花台板胶，使其在保证台板胶的各种特有性能的条件下，将大部分的有 机刺激性溶剂代之以水，从而达到大幅度降低大气污染的目的，并且降低了原料成本。另外， 本文还研究了水溶型丙烯酸酯印花台板胶的合成工艺，同时考察了增稠剂、交联剂、助溶剂 与水的稀释比例等对胶粘剂性能的影响，研制出一种性能优良，价格低廉的改性丙烯酸酯印 花台板胶。 2 实验部分 2.1 实验原料和实验仪器 主要原料：丙烯酸丁酯（BA ），丙烯酸甲酯（MA ），甲基丙烯酸甲酯（MMA ），丙烯酸 （AA ），丙烯腈（AN ），增稠剂