酒钢CSP钢水快速深脱硫技术的开发与实践.pdfVIP

第十五届全国炼钢学术会议文集 酒钢 CSP 钢水快速深脱硫技术的开发与实践 靳旭冉 程子建 （酒钢集团有限责任公司，甘肃 嘉峪关 735100） 摘 要：本文通过对酒钢CSP 钢水脱硫机理和影响因素的分析，对转炉出钢和精炼各环节进行了改进和控制， 使 SS400 等普碳钢平均精炼时间由原来的 75min 缩短到现在的 55min 以内；SPHC 等低碳钢平均精炼时间由 原来的80min 缩短到现在的60min以内，很好满足了快速生产的需要。另外，通过脱硫工艺开发，还降低了 钢铁料消耗，降低了炼钢成本。 关键词：快速深脱硫 白渣 LF CSP The Practice of the Rapid Deep Desulfurization in LF Process for CSP Steelmaking Jin Xuran Cheng Zijian (Jiuquan Iron Steel Corperation(Group),Ltd, Jia Yguan, Gansu, 735100) Abstract: The effecte and mechanism of the LF desulfurization for CSP steemaking were analysed, in JISCO, and the corresponding improves and control measures were taken for the LF and converter process. As a result, the average LF treatment time was reduced to less than 55min from the initial 75 min for the common carbon steel grade such as SS400. and to less than 60 min from the initial 80 min for the low carbon steel grade such as SPHC.Those problems were solved gradually by means of improving the tapping hole maintence method. Additionally, .the index of metal yeild is improved, and the cost of steelmaking is saved through of such desulfurization process. Keywords: rapid deep desulfurization white slag LF CSP 1、前言 酒泉钢铁（集团）有限责任公司二炼钢厂（以下简称酒钢二炼钢厂），由于进精炼钢水硫含量较高， 而CSP连铸浇注钢水要求硫含量极低(硫含量≤80×10-6)，所以酒钢二炼钢厂LF精炼炉担负着比较繁重的脱 硫任务。长期以来，精炼时间长一直是生产的限制性环节。2006 年8月，随着 3炉 3 机的生产，精炼时间 较长的矛盾日益突出。因此进一步开发CSP钢水快速深脱硫技术，缩短精炼时间有着重要的意义。 # # 自 2006 年5月、6 月CSP7、、8 机相继投产以来，酒钢二炼钢厂一直致力于CSP钢水快速深脱硫技术的 开发与研