酒钢二炼钢转炉出钢钢水S含量的预报及影响因素分析.pdfVIP

第十五届全国炼钢学术会议文集 酒钢二炼钢转炉出钢钢水S含量的预报 及影响因素分析 王德勇 程子建 （酒钢（集团）有限责任公司，甘肃 嘉峪关 735100） 摘要：利用炉渣分子结构理论计算出转炉钢渣分配比，确定转炉脱S 能力，根据转炉钢渣分配比可计算出转 炉终点钢水S 含量，实现转炉终点钢水S 含量的预报，并对影响转炉终点钢水S含量的因素进行分析，确定 了S负荷量和钢水增S的临界点，对生产组织具有指导意义 关键词：炉渣分子结构理论，转炉钢渣分配比，转炉出钢钢水 S含量预报，S负荷量和钢水增S的临界点 The Sulfur Content Forecast and the Infulence Factor Analysis for Converter Steelmaking Process, JISCO Wang Deyong Cheng Zijian (Jiuquan Iron Steel Corperation(Group),Ltd, Jia Yguan, Gansu, 735100) Abstract: The sesulfurization capacity of converter steelmaking can be determined by the distribution ratio which is calculted by the salg moleculer structure theory between the melten and the salg. According to this method, the final sulfur content of converter steelmaking could be forecasted, and the infulence factors for the forecast result were analysed. It could be a guide for producing organization by the determination of the sulfur burthen and sulfur increasment critical point Keywords: salg moleculer structure theory distribution ratio of melten and slag final sulfur forecast the sulfur burthen and sulfur increasment critical point 1 现状分析 酒钢炼钢二工序投产后，随着铁水预处理、转炉、精炼各环节的工艺技术的完善并达标，铁水预处理、 LF 精炼的脱S 功能开发并释放出来，转炉在生产过程中的任务得到了简化，转炉脱 S 功能在铁水预处理或 精炼环节完成。但是如何合理的优化工艺、降低消耗，搭配铁水预处理、转炉、精炼的脱 S功能成为主要 问题。尤其是在铁水预处理、LF 精炼的脱 S 功能已明确的情况，转炉作为承上启下的环节，合理并精确的 控制出钢水的 S 含量成为关键。基于以上原因，有必要展开对转炉钢水 S 含量精确预报的研究。 2.转炉脱S状况的调查 2.1 脱 S 反应 [FeS]+（CaO）=[FeO]+（CaS） （O2-）+[S]=[ O]+（S2-） 2.2 炉渣的脱S 能力 2.2.1 炉渣的 Ls 计算 炉渣的脱 S能力由钢渣的分配比确定，根据炉渣的分子结构理论，转炉渣 S 的分配比按如下公式计算 Ls=（S%）/[S%] = （0.5+2.25∑nFeO）[1+（4nCaO+2.5nMnO）/∑nFeO]