水性双组分汽车漆的制备.docVIP

高性能水性双组分汽车清漆的制备 潘明旺（河北工业大学）；贾艳华（天津灯塔涂料工业发展有限公司，300400） 摘要 水性双组分聚氨酯(WB 2K-PU)涂料是环保领域突起的一门新技术，它具有高性能，低VOC含量的特点。随着多元醇树脂和异氰酸酯固化剂的发展，水性双组分聚氨酯涂料已经发展到汽车上的涂装，且具有优异的涂膜性能。本文介绍了2K-PU 涂料中树脂、助剂的选择，并制备了高性能水性双组分聚氨酯汽车涂料。 关键词：2K-PU ；汽车清漆；高性能 Preparation of waterborne two-component automobile coatings Pan MingWang(HeBei university of technology);Jia YanHua (Beacon coatings of TianJin co,Ltd, 300400) Abstract In the field of environmentally friendly coatings waterborne two-component polyurethane (WB 2K PU)systems represent a new technology ,combining the good film properties of solventborne two-component polyurethane coatings with the low VOC values of waterborne technology .Recently, with development of polyol and isocyanate WB 2K PU coating have developed to finishing of high-performance automobile clearcoats which combine good chemical resistance with excellent resistance . In this paper,introducing the choice of resin, aid and preparation of WB 2K PU coatings. Keywords: two-component polyurethane; automobile clearcoats; good film properties 0前言 双组分聚氨酯涂料具有优良的机械性能，涂膜硬度高、附着力强、耐磨性好及突出的耐化学品性、耐候性和低温成膜等特点,广泛应用于工业防护，木器家具和汽车涂饰等方面。随着各国环保法规的健全和人们环保意识的增强，传统溶剂型聚氨酯（SB-PU）涂料中的挥发性有机化合物(VOC)的排放量受到愈来愈严格的限制，开发低污染、高性能、多功能的环保型水性涂料成为涂料技术发展的主要方向。在我国，水性底漆和水性中涂漆已经成功地应用于汽车领域，随着水性涂料的发展，水性双组分聚氨酯涂料作为一种低污染、工艺清洁的环保涂料，已经成功的应用于汽车面漆及修补漆，它将溶剂型双组分聚氨酯涂料的高性能和水性涂料的低VOC排放相结合，成为涂料工业研究的热点。 1 原材料的选择 水性双组分聚氨酯清漆是由羟基组分、异氰酸酯组分、助剂、及水组成。在汽车罩光清漆中，主要包括以下组分： 1.1?含羟基组分在水性双组分聚氨酯涂料中?,?使用的含羟基多元醇有、聚酯、聚醚、聚氨酯水分散体等1.1.1水分散性羟基丙烯酸树脂??羟基丙烯酸树脂可用溶液聚合的方法得到。首先在反应器中加入有机溶剂?,?升温并保持在一定温度下?,?滴加含有羧基、羟基的丙烯酸酯单体和引发剂等的混合物?,?反应完全后?,?降温?,?减压蒸馏除去部分或全部溶剂?,?加入中和剂和水得到。将其与各种添加剂混合后?,?再与常规溶剂型脂肪族聚氨酯固化剂组成水性双组分聚氨酯涂料???? 1.1.2羟基丙烯酸树脂的选择 水性双组分聚氨酯涂料的多元醇必须具有良好的分散性,即以尽量低的剪切能耗将憎水的多异氰酸酯固化剂很好的分散在水中，羟基丙烯酸树脂的选择是极其重要的，和溶剂型双组分聚氨酯涂料相比，羟基组分不仅参加交联反应，而且影响其在水中的分散性。通过设计合成配方，可以获得理想的涂膜。羟基丙烯酸树脂的羟值，酸值，玻璃化温度及其中和度决定其水溶性和最终的成膜。改变树脂技术指标的影响因素： ⑴ 羟值提高，水溶性增加，涂膜干燥慢，光泽降低，耐化学品性、耐水性变差。 ⑵ 酸值提高，水溶性增加，涂膜干燥快，附着力、柔韧性提高，耐水性、化学品性差，光 泽降低。 ⑶ 玻璃化温度提高，对水溶性影响