High-strength Steel under Monotonic and Cyclic Loading –A Study on the Damage Evolution near the Edge of a Stamping Tool.pdfVIP

High-strength Steel under Monotonic and Cyclic Loading – A Study on the Damage Evolution near the Edge of a Stamping Tool P. J. Gruber, G. Jesner, R. Ebner und O. Kolednik The paper deals with damage evolution near cyclically loaded edges of stamping or cutting tools. A specific cyclic edge-loading test procedure has been developed for characterising the behaviour of edges that are subjected to cyclic loading under high compressive mean stress. With this procedure, the local deformation behaviour and the damage evolution can be analysed after different load cycles. A cold work tool steel grade K340 Isodur produced by electroslag remelting technology was investigated. Hochfester Werkzeugstahl unter monotoner und zyklischer Belastung – Eine Studie über die Schädigungsentwick- lung an der Kante eines Stanzwerkzeuges. Die Arbeit konzentriert sich auf die Schädigungsentwicklung an zyklisch hochbelasteten Kanten von Stanz- oder Schneidwerkzeugen. Zur Untersuchung der Schädigungsentwicklung wurde ein zyklischer Kantenstauchversuch entwickelt, mit dem Belastungen ähnlich jenen von Kanten von Stanzwerkzeugen simuliert werden können. Mit diesem Test wurden das lokale Verformungsverhalten und die Schädigungsentwicklung nach verschiedenen Lastzyklen analysiert. Die Tests wurden an einem nach dem Elektroschlacke-Umschmelzverfahren hergestellten Kaltarbeitsstahl des Typs K340 Isodur durchgeführt. 1. Introduction residual stress occurs near the edge, depending on the edge geometry, the parameters of the stamping process, A variety of different tool steels, ranging from low-alloyed and the tool and workpiece materials5,6 . Re