李亮-一种高强度合金灰铁的工艺控制(需修改).doc

请用特殊颜色的字进行修改！ 一种高强度合金灰铁的工艺控制 1齐齐哈尔市精铸良铸造有限责任公司 161004 李亮 王彬 鲍玉龙 [摘要] 灰铁通常具有良好的减震和吸收震动的功能，加入了一定的合金和特殊的热处理后，灰铁在此基础上又增加了耐磨、耐腐蚀等功能；同时因为金相组织为奥贝氏体，又具有类似球墨铸铁的延展性和韧性,我公司接到一种美国铁路货车配件斜楔产品 ，要求材质为奥贝氏体高强度合金灰铁，金相组织为奥贝氏体。该产品对材质的化学成分、金相组织、硬度值都有严格的要求。该产品的研制成功拓宽了灰铁的使用范围，为公司稳定美国铁路货车产品配件市场又增加了技术储备。 [Abstract] iron usually has good shock absorption vibration function, add a certain alloy and special heat treatment, gray iron on the basis of this increased resistance to abrasion, corrosion and other functions; at the same time, because the microstructure of Aobeishi body, and with similar ductile cast iron, malleable and ductile, our company has received an American railway truck accessories wedge product, material required for Austempered bainite high strength alloy cast iron, microstructure of Aobeishi body. The chemical composition, microstructure, hardness of the material values have strict requirements. The success of the product and the use range is widened gray iron, is stable for the company the United States railway freight car accessories market and increase the technical reserves. 材料说明 灰铁通常具有良好的减震和吸收震动的功能，加入了一定的合金和特殊的热处理后，灰铁在此基础上又增加了耐磨、耐腐蚀等功能；同时因为金相组织为奥贝氏体，又具有类似球墨铸铁的延展性和韧性。 本材质就是一种高强度合金灰铁，要求石墨形态为A-E型石墨，热处理后金相组织为奥贝氏体，布氏硬度为HBW340-400，延伸率为4-7%，抗拉强度大于600MPa,该材质被应用在美国铁路货车摩擦片上，配件名称为斜楔 ，主要作用为耐磨、减震。（1.请补充铸件照片和斜楔用途说明！ 2.文中提到的整体淬火的铸件，请交代铸件壁厚是多少，因为壁厚与合金加入量相关！ 3.材料要求没有交代清楚，既然增加耐蚀和延展性，那么有具体验收指标吗？还是仅要求硬度牌号？ 订货要求的验收指标有哪些，数值是多少？请一一列出！） 熔炼生产工艺的控制 1） 主要炉料为熔炼生铁Q10（加入比例为60%）、球铁回炉料（加入比例为20%）、碳素钢（废钢加入比例为20%）；加入主要合金为钼铁（加入比例为1.5-1.8%）、电解铜（加入比例为2-2.2%）和高效硅钡孕育剂（加入比例为0.9-1%）。冶炼过程为：1）、向中频炉中依次加入Q10生铁150公斤，回炉料50公斤，废钢50公斤。2）、升温熔化至液体状态时，加入钼铁（Mo含量60%）3.75公斤，电解铜（Cu含量99.99%）5公斤，继续升温至1440-1460℃时，静止2分钟后出炉。3）、在包底加入高效硅钡孕育剂（Si 46%（Si含量是0.46%吗？请核实！）、Ba3%)2.5公斤，净化剂（主要成分 CaO、Al2O3）：1公斤，将铁水冲入包中，加入火山灰除渣剂1.5公斤，充分扒渣后即可进行浇注。4）、浇注温度控制在1350-1400℃为宜。 （请将上述加入的炉料以及孕育剂折算成总质量的百分比，不要写成公斤！） 孕育处理的必要性 实践证明，灰铁中石墨分布越细小均匀，强度、硬度