Chapter 3 Man made fibers 化学纤维 Fibers are either made by nature or by man. The development of man-made fibers was generated by a desire to make fibers without the deficiencies of the natural fibers. An example is a fiber with natural wash-and-wear properties. Another example is a fiber that is very strong and also has excellent wearability. All man-made fibers are produced originally as filament fibers. Sometimes they remain so, but often they are made into short lengths from 1-1/2 to 6-1/2 inches. When this occurs, the fibers are called staple fibers. 3.1 化学纤维的分类 1）按高聚物的来源分??：? ??① 再生纤维：是以天然聚合物为原料，经过化学和机械方法制成的，化学组成与原高聚物基本相同的化学纤维。 ??② 合成纤维：以石油、煤、天然气及一些农副产品等低分子作为原料制成的单体后，经人工合成获得的聚合物纺制成的化学纤维。 （2）按内部组成分 ??① 聚酯纤维 （PET） 聚对苯二甲酸乙二酯纤维 (涤纶)(大可纶) ??② 聚酰胺纤维（PA）(锦纶)(尼龙)?? ③ 聚丙烯腈纤维（PAN）(腈纶) ??④ 聚乙烯醇缩甲醛纤维（PVA）(维纶) ??⑤ 聚丙烯纤维（PP）(丙纶) ? ⑥ 聚氯乙烯纤维(氯纶) ??⑦?聚氨酯纤维(氨纶) 按形态结构分 ①?长丝：化学纤维加工的连续丝条，不经过切断工序。又分为单丝、复丝与变形丝。 ② 短纤维：化纤在后加工中切断成为各种长度规格的短纤维。(30-40棉)(70-150毛)(51-65中长) ?③ 异形纤维：是指经一定几何形状（非圆形）喷丝孔纺制的具有特殊截面形状的化学纤维。 ④ 复合纤维：由两种及两种以上聚合物，或具有不同性质的同一聚合物，经复合纺丝法纺制成的化学纤维。分并列型、皮芯型和海岛芯等。 ⑤ 超细纤维：指单丝线密度较小的纤维，又称微细纤维。 根据线密度范围又可划分为： 细特纤维(0.44～1.11dtex)；超细特纤维（0.011～0.44dtex） 按用途分： ??① 普通纤维： ? ② 特种纤维：是指具有特殊的物理化学结构、功能或用途的化学纤维，其某些技术指标显著高于常规纤维。 ??????包括： 1、具有特殊力学性能的纤维 ??????????? ??2、具有特殊热学性能的纤维 ??????????? ??3、具有化学稳定性的纤维 ??????????? ??4、具有特殊物理性能的纤维 ????????? ????5、具有特殊物化性能的纤维 ????????? ????6、具有特殊生物性能的纤维 　如：耐高温纤维、耐辐射纤维、高湿高模纤维等。 3.2 化学纤维的制造 一般经历三个过程：纺丝液的制备——纺丝——后加工 （1）纺丝液的制备 熔体法：将高聚物加热到熔点以上，使其熔融成较稳定的粘性流动的纺丝熔体。 如：涤纶、锦纶、丙纶、乙纶。 ?原因：熔融温度＜分解温度 ?溶液法：用适当的溶剂将高聚物溶解成具有一定粘度的纺丝液。? 如：粘胶纤维、醋酯纤维、腈纶、氯纶、维纶。 ?原因：熔融温度＞分解温度 （2）纺丝 ?? ?熔体纺丝：使熔融的成纤高聚物熔体从喷丝头细孔中喷出在周围空气中（或水中）冷却凝固成丝的方法?。 ??????? 优点：过程简单、纺丝速度高。? ??? 溶液纺丝有： ? ? 溶液纺丝有： a.湿法纺丝： ????????? 纺丝液从喷丝头喷出后在液体凝固剂中固化成丝方法。例：粘胶、腈纶。 ??????? 特点：喷丝孔数多、速度慢。? b.干法纺丝： ??????? ? 纺丝液从喷丝头喷出后，在热空气因溶剂迅速挥发而凝固成丝的方法。 例：维纶、醋酯纤维?。 ??????? 特点：质量好、成本高、易污染环境（较少采用）。 3）后加工 目的：使纤维具有一定物理机械性能（强力、伸长、抗静电、抱合力等）。 因为初生纤维(刚从纺丝机上下来的纤维) 未经过拉伸、热定型等后加工过程，内部结构不稳定。所以强度低、伸长大、弹性差，不具有纺纱价值