新型建筑功能材料.docVIP

脱硫石膏基加气混凝土 (武汉理工大学，国家重点实验室，武汉430070，中国) [摘要] 本文通过对影响免蒸压脱硫石膏基加气混凝土抗压强度、体积密度和浇筑稳定性的水胶比、料浆温度及养护条件等因素的研究，得出不同的养护条件对制品的强度影响很大，而且粉煤灰、水泥、生石灰等原料的掺量和养护条件都存在一个最佳值和最佳范围，只有其达到最佳掺量和最佳范围时，才能确保免蒸压脱硫石膏基加气混凝土的性能最好。 [关键词] 脱硫石膏，加气混凝土，免蒸压，节能 FGD gypsum—based aerated concrete Han Wei Wei (Wuhan University of Technology, State Key Laboratory, Wuhan430074, China) Abstract：Based on the impact from the desulfurization gypsum based autoclaved aerated concrete compressive strength, volume density and casting of the stability of the water-binder ratio, pulp temperature and maintenance condition of the factors such as research, come to different maintenance condition of the strength of the products impact, and fly ash, cement, lime, the mixed quantity of raw materials and maintenance condition has a best value and the best range, only to the optimum content and the best range, can ensure that exemption autoclaved aerated concrete desulfurization gypsum and the performance is the best. Keywords : FGD gypsum,aerated concrete, non—autoclaved, Energy—saving 前言 脱硫石膏粉煤灰制品具有节能、环保、隔音、隔热等良好性能；加气混凝土具有轻质、利废、保温和节能的优点。近些年来，无论是对于脱硫石膏粉煤灰制品的研究，还是加气混凝土的研究，国内外都已取得了丰硕的成果。但是在它们的生产过程中，存在着耗能过多，污染大等现象，没有达到节能环保的要求，当然也不利于其长远的发展，并且国内外对于脱硫石膏基加气混凝土的研究还相对较少，因此对于耗能少，又环保的免蒸压脱硫石膏基加气混凝土的研究变得十分必要。这不仅将实现节能减排的要求，而且更利于其的长期发展[1 2 3]。 1原料选择 实验主要原料包括：脱硫石膏、粉煤灰、水泥熟料、生石灰和一些试验所用的其他化学试剂（比如发气剂、缓凝剂等）。 ①粉煤灰：Ⅱ级粉煤灰，筛余为0.38%（80μm筛），比表面积为470㎡/㎏。 ②水泥：P.O42.5，相对密度为3.10，比表面积350㎡/㎏。 ③生石灰：磨细至4900孔/cm3筛的余量13%，有效CaO含量为78%，消化时间5—10min。 ④脱硫石膏的相关参数如下表1—1。 表1—1 脱硫石膏 参数 烧失量 标准稠度用水量 初凝时间 终凝时间 抗压强度 脱硫石膏 2.7 0.65 6min 12min 13MPa ⑤发气剂和稳泡剂：铝粉和铝粉脱脂稳泡剂 ⑥混凝剂：柠檬酸钠 2实验方法 ⑴石膏及其复合胶结材的标准稠度用水量、流动度损失（50s,120s），凝结时间、强度测试按GB97776-88《建筑石膏》规定的方法实验[4]。 ⑵脱硫石膏基加气混凝土材料的干体积密度的测定主要步骤：将试件放入电热鼓风干燥箱内，在45±5℃下烘至恒重，即一般再进行24h烘干后冷却至室温称重。 ⑶抗压强度的测定采用WE-30型液压式万能材料试验机测定制品的破坏载荷，按GBJ81-85《普通混凝土力学性能实验方法》进行测定[5]。 ⑷采用XRD和SEM等测试方法对制品的微观结构进行研究，进而从微观来解释宏观的现象。 3实验研究 3.1粉煤灰掺量对脱硫石膏基加气混凝土性能影响的研究 混凝土配制中加入粉煤灰，不仅能降低混凝土材料的成本，而且也能降低混凝土的水化热，提高混凝土的抗渗和抗腐蚀等性能,节约了水泥用量[]。而且马海英等的研究也表明，当粉煤灰添加到混凝土中后，