al2o3caosio2系轻质耐火材料的制备及性能分析word格式论文.docx

phaseanalysisoflight-weightrefractorycastableshavecorundum,anorthite,mullite andglassphase,withtheusingtemperatureabout1450℃,andcanbeusedinliningofthe industrial furnacedirectlycontact with the flame.Industrialalumina,aluminumhydroxide,Guangxiwhitemud,kyanite,lightcalcium carbonate,induwtrialgypsumwereusedasrawmaterialsinthelight-weightrefractory brickspecimens,withpolystyreneballs,sawdustandcarbonblackascomplex pore-formingagents,whichtotaldosagecontrolledabout16%,whenthe adding amountofpolystyreneballswith1%,sawdustwith2%,andtheblackcarbonwith13% thecompressivestrengthofobtainedsampleis1.96MPa.Changesinformulationonthe basis,whentherelativecontentofanorthiteis32%,thebulkdensityoftheobtainedsampleis1.15g/cm3,compressivestrengthof2.19MPa.Thematerialcanbeusedforworkingtemperature at about 1500℃ in the furnace.Keywords：light refractory;pore-forming agent;anorthite;mullite;corundom目录1引言............................................................................................................................12文献综述....................................................................................................................22.1轻质耐火材料的概述..........................................................................................22.1.1轻质耐火材料的分类标准...........................................................................22.1.2轻质耐火材料的性能指标...........................................................................32.2轻质耐火材料的生产方法..................................................................................52.2.1化学反应法...................................................................................................62.2.2泡沫成型法...................................................................................................62.2.3可燃物加入法...............................................................................................62.2.4多孔材料法...................................................................................................72.3轻质耐火材料的隔热机理......................