基于应变梯度塑性理论的微纳米尺度材料力学行为分析-mechanical behavior analysis of micro-nano scale materials based on strain gradient plasticity theory.docxVIP

1、Threedifferentinterfacemodelsareproposedwithinthestraingradienttheoryframeworkdependingonthedeformationcharacteristicsofthemicro/nano-sziedmaterials.Inthecompressedsinglecrystallinemicropillar,theinterfacesliebetweenthesliplayerswhichareindifferentdeformationstatusduetoasynchronousplasticyieldinginthemicropillarandplayaroleasthetransitioninterfaces.Inthecompressedbi-crystallinemicropillar,thegrainboundaryplayaroleasbarriertothemovementofdislocations,andtheinterfaceenergyisendowedtothegrainboundarywithinthestraingradientplasticityframework,thentheinterfacialyieldingrulesaredeveloped.Innanocrystallinesolids,grainboundariesoccupysignificantvolumefractionofthematerial,thusaretreatedasaseparatephaseendowedwithbalanceequationsandconstitutiveequations.2、Basedonthestraingradientmultilayermodel,the“strainbursts”phenomenaobservedinsinglecrystallinemicropillarcompressionexperimentsareinvestigated.Thehigher-orderstress,whichisdiscontinuousattheinterfacebetweenaplasticlayeranditsneighboringelasticlayerbutcontinuouswhentwoneighboringlayersbegindeformingplastically,istheunderlyingmechanismresponsibleforthestrainburst.Thetransitionfromdiscontinuitytocontinuityofthehigher-orderstressacrosstheinternalboundarybetweentwoneighboringlayersresultsinthestrainburst.Furthermore,thestress-strainresponseofthesinglecrystalmicropillarisdispersed;thestraingradientmultilayermodelcouldalsocapturetheupperandlowerboundsofthestress-straincurves.3、Thecompressionbehaviorofthebi-crystallinemicropillarisinterpretedbyconsideringtheinterfaceenergyterminthegrainplasticityframework.Grainboundaryistheinterfacewherehigherorderstressexperiencesajump,thusitismodeledusinginterfaceenergy,an“interfacial”yieldcriterionisdeducedtodescribetheyieldingbehaviorofgrainboundaryasaresult.Thetri-linearstress-straincurvesobtainedfromthetheoryfitinwellwithexperimentaldataofbi-crystalmicropillars,anddisplaytwodistinct“knee”atwhichthegrainandgrainboundarybegintoyield.4、Themechanicalbehaviorofthenanocrystallineisanalyzedusingthe