专科毕业论文 含硫原油加工过程中的硫腐蚀.doc

含硫原油加工过程中的硫腐蚀 摘要：结合石油化工设备硫腐蚀的特点，从3个方面对炼油厂的硫腐蚀问题进行了理论分析与简述。从硫腐蚀现状来看，已经对炼油设备造成了严重腐蚀，而且贯穿于炼油的全过程；从机理来看，硫腐蚀类型较多、过程比较复杂，许多机理性问题还远远没有研究清楚；从目前实际情况看，应加强对硫腐蚀机理的研究，弄清硫腐蚀的规律，为控制原油加工过程中的硫腐蚀提供理论基础。 关键词：高硫原油 设备 控制 腐蚀 Abstract: combining petrochemical equipment characteristics of sulfur corrosion, from three aspects of the refinery sulfur corrosion problems were analyzed in theory and briefly reviewed. Judging from sulfur corrosion situation of refining equipment, has caused a serious corrosion, and throughout the whole process of refining; Judging from mechanism, sulfur corrosion type more, process more complicated, many machine rational problem is far from research clear; From the actual situation look, should strengthen the research of the corrosion mechanism of sulfur, make clear the pattern of sulfur corrosion control processing crude oil provides the theoretical foundation of sulphur corrosion. Keywords: sour crude equipment control corrosion 目录 第1章概述 第2章原油中的硫和硫化物 2．1含硫化合物的存在形态及分布 2．2活性硫 2．3含硫原油炼制过程中活性硫的由来和形成 第3章活性硫腐蚀的主要过程和腐蚀机理 3．1活性硫腐蚀的主要过程 3.2进口原油腐蚀性介质调查情况 第4章国内加工含硫原油的防腐蚀工作 4．1规范防腐蚀管理 4．2材料表面技术改性开发 4．3 防腐蚀技术的创新 4．4今后应开展的工作 第5章 加工含硫原油设备存在的隐患 5.1常顶空冷器泄漏 5.2减压渣油换热器发生自燃 5.3焊缝发生开裂泄漏 5.4膨胀节开裂 5.5空冷器出口法兰焊缝开裂 5.6法兰密封垫圈开裂 5.7加氢精制汽提塔顶回流罐内壁裂纹 5.8螺栓断裂事故常有发生 5.9球罐出现微裂纹 5.10烟气露点腐蚀 5.11油罐腐蚀 5.12自燃 第6章常规的防腐蚀措施 6．1 工艺防护 6．2材质升级 6．3实时在线监测 6．4防腐结构优化设计 第7章 国内外对加工高硫原油腐蚀控制情况 7．1 强化工艺防腐蚀技术 7．2合理选材 7．3强化监测技术 第8章建议 第9章结束语 第一章概述 随着国内沿海地区从中东、西北地区从中亚进口含硫原油数量的大幅度增加，以及国内含硫油田的开发，原油平均含硫量逐年增高(见表1、表2)。从目前的原油产量看，含硫原油(含硫O．5％一2．0％)和高硫原油(含硫大于2％)的产量已占世界原油总产量的75％，其中含硫大于2％的原油占30％。原油硫含量的增加，使加工高硫原油的设备，包括进口的不锈钢设备和管道，发生严重的硫腐蚀。据报导常压加热炉回弯头腐蚀速率可达6眦n／a【l|，cr5Mo合金管的腐蚀速率为1．7—21．1眦n／a。正常生产中由于硫腐蚀时常引发破裂、燃烧、爆炸等恶性事故，同时还导致严重的环境污染。 表1 中国石化集团进口原油情况 年份 1999年 2000年 2001年 预计 2010年 预计 进口原油量 /Mt 5.94 14.16 23.60 50.00-60.00 表2中石化茂名分公司加工原油情况 年份 1998年 1999年 2000年上半年 原由加工量/MT 7.22 8.16 5.27 含硫原油比例/% 37.31 35.82 53.03 高硫原油比例/% 2.876 8.56 22.66 原油平均含硫/w% 0.5937 0.7718 1.214