聚丙烯酸铵在超细硫酸钡制备中的分散作用.pdf

豆 丁 推 荐 ↓ 精 品 文 档 (化学工程联合国家重点实验室(清华大学) ，北京100084) 摘要：以聚丙烯酸铵为分散剂，采用直接沉淀法，制备超细BaSO4 。考察了分散剂用量，反 应体系pH 等因素对BaSO4 粉体分散效果的影响。用TEM 和BET 比表面积分析仪对粉体进 行表征。碱性环境下，聚丙烯酸铵加入量相当于BaSO4 理论质量的10%时，分散效果较好， 可得到粒径小于200nm ，比表面积大于50m2/g 的超细BaSO4 粉体。该条件下，超细BaSO4 颗粒形貌为椭球形，粒径均一，分布较窄。并对聚丙烯酸铵的分散机理进行了分析。 关键词：分散剂；超细硫酸钡；聚丙烯酸铵 中图分类号：TQ027 文献标识码：A 文章编号： The Dispersive Effect of PAANH4 in the Preparation of Ultrafine Barium Sulfate ZHOU Hong zhao ，Wu Guo hua ，ZHU Shen lin (State Key Laboratory of Chemical Engineering ，Tsinghua University, Beijing100084, China) Abstract: Ultrafine barium sulfate was prepared by direct precipitation method, with PAANH4 as dispersant. The effect of the amount of PAANH4 and the pH of reaction system on dispersion of BaSO was investigated. While the mass addition of PAANH was 10% of barium sulfate in theory 4 4 and the environment was alkaline, better effect could be obtained. The particle size was less than 2 200nm and the specific surface area was more than 50m /g. Under this condition, the morphology was ellipsoidal and uniform particles could be prepared. The mechanism of dispersion was also analyzed. Key words: dispersant ；Ultrafine barium sulfate ；PAANH4 引言 硫酸钡（俗称重晶石）是一种重要的无机化工产品，具有高比重（4.5g/cm3 ）、对X 射 线的不透明、惰性及纯白等特性，在涂料和塑料中可以作为填充剂和添加剂，也可用作医学 表征[1] ；硫酸钡耐高温、耐酸、耐碱，作为添加剂可以改善材料的抗冲击、防腐蚀、抗高温、 空间稳定等性能[2] 。对重晶石进行精细加工，或利用化学法生产出超细、超白、表面改性的 硫酸钡已成为硫酸钡行业的主要方向。液相法是目前实验室和工业上最为广泛使用的制备超 细粉体材料的方法[3] 。液相法制备粉末过程中的最大的问题就是粉末的团聚。为了得到分散 良好的颗粒，需要在反应体系中加入分散剂。 聚丙烯酸盐是聚电介质，具有很长的分子链，在一定的条件下充分电离，加入反应体系 中，其长分子链能够起到空间位阻作用，表面电荷能够起到静电稳定作用，是一种很好的分 [ CH2 CH CH2 CH ] n 散剂。聚丙烯酸铵是常用的聚丙烯酸盐，其分子式为 COONH