注塑模具FLASH.docVIP

FLASH ? ?Flash can be defined as excess plastic material forced out of the cavity. This occurs at any point where two mold surfaces meet. Machine Excessive Residence Time In Barrel Explanation: Ideally, a shot size should equal 50% of the capacity of the barrel. That results in processing one cycle while preparing for the next cycle. However, this is a general statement because, depending on the material, the ratio can be as small as 20% for non-heat-sensitive materials such as polypropylene and up to 80% for heat-sensitive material such as PVC. As the ratio drops, the time of residence by the material in the barrel increases, and the material gets hotter. It will flow much easier at this point and enter areas where it could not at its normal viscosity. This results in a flashing condition in those areas. Solution: Strive for a 50% shot-to-barrel ratio. This is ideal but can go as low as 20% if the material is not too heat sensitive (like polypropylene) and up to 80% if the material is extremely heat sensitive (like PVC). It is not a good idea to empty the barrel every shot because more time will be required to bring the next mass of material up to proper heat and degradation may occur. Excessive Injection Pressure Explanation: If too much injection pressure is used, the clamp unit may not be able to hold the mold closed, especially on a machine with a hydraulic clamp. The mold will blow open and plastic material will leak out around the perimeter of the parting line. This leakage is called flash. It can also occur between any mating steel surfaces of the mold such as around ejector pins and slides. Major mold damage may occur as a result of flashing. Solution: Reducing the injection pressure reduces the tendency for the material to flash. In addition, make sure there is a properly raised shutoff land around the perimeter of the cavity. This will focus the clamp force and allow less clamp tonnage to be used. Without the shutoff land on the mold, the machin