碳钢阀门外防腐涂层物理机械性能检验方法与仪器[权威资料].docVIP

碳钢阀门外防腐涂层物理机械性能检验方法与仪器 　　Test Method and Instrument of Outer Anticorrosive Coating Physical 　　and Mechanical Properties of Carbon Steel Valves 　　Huang Jun 　　（Shaanxi Radio TV University，Xian 710068，China） 　　摘要：外表面防腐涂层性能是非耐腐金属工业阀门的重要质量指标，本文从制造厂生产实际出发，着重介绍并推荐适合车间现场应用的碳钢阀门外防腐涂层干膜厚度、附着力、孔隙率等物理机械性能的检验方法以及相应的检测仪器。 　　Abstract： Outer anticorrosive coating physical and mechanical properties are important quality index of non-corrosion resistance industrial valves. This article begins with actual manufacture, focuses on and recommends test method and instrument of anticorrosive coating physical and mechanical properties such as dry film thickness, adhesion and porosity of carbon steel valves, which suits site application in workshop. 　　关键词：外表面防腐涂层 物理机械性能 检验方法与仪器 碳钢阀门 　　Key words： outer anticorrosive coating；physical and mechanical properties；test method and instrument; carbon steel valves 　　TH134 A1006-4311（2011）19-0047-02 　　0引言 　　工业阀门是我国通用机械行业的重要分支产品，广泛运用于对固、气、液等单相或混相流体介质的开关、流量控制领域。阀门属于承压设备类，出厂前要逐台进行全面的质量检测与性能试验，包括材质检验、壳体承压性能试验、正反向高低压力密封性能试验以及其他如耐火、低温、扭矩、流阻试验等以充分检查设计结果的正确性与运行可靠性。对于非耐腐金属阀门如普通铸碳钢、锻碳钢、铸铁阀门而言，影响其使用性能与寿命的质量要素除了设计水平、部件材料的品质与性能、加工与装配精度等，还需特别关注其内外表面的防腐涂装性能。涂层的化学组分性能与结构体系一般由涂料厂商推荐与保证，故本文结合国内阀门行业中小型制造企业生产现状，试对碳钢阀门外防腐涂层物理机械性能检测与试验方法以及相应的仪器设备保障措施作一讨论。 　　1碳钢阀门外防腐涂层主要性能指标 　　本着方便车间现场试验以保证生产进度安排并尽可能体现防腐涂层质量优劣水平的原则，碳钢阀门外防腐涂层物理机械性能试验主要指标宜包括涂层干膜厚度DFT(Dry film thickness)、附着力、孔隙率三项，而其他如气液渗透率、耐候率、耐酸耐碱耐油率等指标则由于测试周期较长一般不适合作为生产性质量检验指标。 　　2DFT值检验方法与仪器 　　涂层干膜厚度直接决定阀体防腐蚀涂层体系的使用寿命，是涂装质量检验的基础性指标，当阀门装置涂层配套体系和运行的外部环境腐蚀条件确定后，涂层厚度即与阀门使用寿命呈正相关关系，当然涂层也不是越厚越好，高DFT会带来施工困难、涂层固化不均、应力开裂等问题，因此需保证碳钢阀门外防腐涂层DFT值处于合理范围。 　　2.1 检验方法涂层干膜厚度测量分为破坏性测量和无损测试两种。破坏性测量法首先对涂膜层进行剖面垂直切割，然后使用光学读数显微镜或机械式直读测微计测量，可准确测出涂膜总厚度和分层厚度，多运用于贸易争议仲裁取证，但显然不适合阀门厂用于生产线制成品涂层质量检查。无损测试方法根据测量原理和适用范围的不同可分为磁力测试法、电磁感应测试法、电涡流测试法、超声测试法和射线透视测试法，超声波和射线透视测试法仪器设备精密昂贵，操作规程繁琐复杂，环境安全法规限制严格，要求人员持有特种作业证，车间现场极少应用，前三种是常用的碳钢阀门涂层无损测厚方法。 　　2.2 磁力测厚法基本原理与仪器根据永磁体与导磁碳钢工件表面间的吸力大小取决于两者距离，磁力式测厚仪测出