大体积砼施工技术浅析.docVIP

大体积砼施工技术浅析 　　摘要：大体积砼具有形体庞大、混凝土数量较多、工程条件复杂、施工技术和质量要求高、混凝土绝热温升高和收缩等特点。大体积混凝土经常出现的问题不是力学上的结构强度，而是混凝土的裂缝。如何防止大体积砼的开裂，如何在施工组织和施工技术上采取必要的措施并加强施工过程的管理和后期养护是我们探讨的重点！ 　　 关键词：大体积混凝土；砼；施工技术； 　　Abstract: The large volume of concrete, concrete with huge quantity, complicated construction condition, construction technology and high quality requirements, increase concrete adiabatic temperature and shrinkage characteristics. The structural strength of large volume concrete often the problem is not mechanical, but concrete cracks. How to prevent concrete cracking, how in the construction organization and construction technology to take the necessary measures and to strengthen the management and maintenance of construction process is the focus of our study! 　　Key words: mass concrete; concrete; construction technology; 　　中图分类号：TU74 　　前言 　　 近几年，随着建行业的迅速发展，高层建筑物，高耸结构及大型设备基础大量的出现大体积砼已经被广泛应用，大体积砼与普通钢筋砼相比，具有结构厚，体形大，钢筋密，砼数量多，工程条件复杂等特点。大体积砼裂缝是大体量混凝土水泥水化热所产生的温度、收缩变形导致的裂缝，必须控制这种裂缝现浇混凝土结构。 　　1 基础大体积砼的特点与裂缝产生的原因 　　 1.1砼强度级别高，水泥用量较大，收缩变形大，产生裂缝 混凝土体积越大，水泥总用量相对大，水泥水化产生的热量越不易散发，温升越高，引起的体积变化也越大。大体积混凝土浇注后，内部温度远较外部高，形成较高的温差，造成内涨外缩，使构件表面产生很大拉应力以至开裂。对于大体积砼施工阶段来说，由于温度变形而引起的裂缝，可称为“初始裂缝”或“早期裂缝”。 　　 1.2受约束，产生拉应力，产生裂缝 　　 体积变化受约束会产生内应力。约束条件有两种，即外约束和内约束。外约束是指结构物的边界条件，一般指基础或其他外界因素对结构物的约束，水泥水化后期，散发热量大于放热量，??件温度降低，体积收缩，受边界条件约束，产生拉应力。如现在比较常见的地下室桶式结构、剪力墙结构受基础约束明显。内约束是由于内部水泥水化热不易散发，表面则易于散发，内部体积膨胀，表面则体积收缩（特别是遇气温骤降或过水），受内部约束，产生拉应力。这时产生的一般是表面裂缝。 　　 1.3抗拉能力低，产生裂缝 　　 混凝土是脆性材料，抗压能力较高，抗拉能力较低。抗拉强度仅为抗压强度的1/10左右；极限拉伸也很小，通常不足1×10－4。大体积混凝土温度变形受约束时产生的拉应变（或拉应力）很容易超过极限拉伸（或抗拉强度）而产生裂缝。大体积混凝土结构设计中，通常要求不出现拉应力或只出现很小的拉应力，但施工中，大体积混凝土结构由于温度的变化而产生很大的拉应力，要把这种温度变化所引起的拉应力限制在允许范围以内是非常困难的。 　　 2 控制温度裂缝发展的基本措施 　　 2.1 基础大体积砼的材料选择与质量要求 　　 水泥。施工中应选用水化热较低的水泥以及尽量降低单位水泥用量(每减少10kg水泥，降低温度1℃)。本工程由于货源限制选用525号普通砼酸盐水泥。粗细骨料。粗骨料选用5～40mm单粒级卵石。细骨料采用中粗砂，其细度模数为218。降低混凝土的干缩。 　　 混合料及外加剂。混凝土中掺入水泥重量0.25%左右的木质素磺酸钙，可明显延缓水化热释放的速度，推迟水化热峰值的出现；同时可减少10%拌和用水，节约水泥，降低水化热。混凝土中掺入适量粉煤灰，不仅改善混凝土的工作度，减少混凝土的用水量，减少泌水和离析现象；同时代替部分水泥，减少水化热。掺入适量UEA膨胀剂，有效地补偿混凝土