浅析粉煤灰综合利用.docVIP

浅析粉煤灰综合利用 　　摘要：从降低粉煤灰对环境污染和将其变废为宝的角度,综述了国内外对粉煤灰综合利用的现状,并具体介绍了粉煤灰在建材制品、化学工业、农业以及环境保护等领域应用中的研究热点,提出了大量的可行方案,为粉煤灰综合利用的全面推广奠定了一定的理论基础。另外还对粉煤灰应用中面临的问题提出了一些应对措施,最后对粉煤灰今后应用的重点作了展望。 　　 　　关键词：粉煤灰的综合利用 　　Abstract: from the lower to the environment pollution of fly ash and its point of view, waste at home and abroad are reviewed in this paper, about the present situation of comprehensive utilization of fly ash and fly ash are introduced in the concrete building materials products, chemical industry, agriculture and environmental protection in areas such as application of the hot research topic, a large number of feasible solution is put forward, for the comprehensive promotion of comprehensive utilization of fly ash has laid a theoretical foundation. Also are faced with the problem in the application of fly ash puts forward some countermeasures, the final key prospected for the future application of fly ash. 　　 　　Key words: the comprehensive utilization of fly ash 　　中图分类号：TU522.3+5 文献标识码：A文章编号： 　　 　　1.煤粉灰概述 　　根据粉煤灰理化性能的不同，粉煤灰综合利用领域包括：混凝土、砂浆应用；水泥应用；新型墙体材料应用；粉煤灰陶粒应用；粉煤灰提铝等高附加值产品；工程回填用灰等方面，提出以下建议。 　　粉煤灰综合利用是指：以粉煤灰为原料生产建材产品、化工产品、复合材料等各类型产品；从粉煤灰中进行物质提取的加工利用过程；粉煤灰用于建筑工程、筑路、农业、回填等工程。 　　济南市粉煤灰主要是由二氧化硅粉、三氧化二铝、氧化钙、烧失量（未燃尽的有机质）、三氧化硫、氧化镁、氧化铁等成分组成，其中主要成分为二氧化硅和三氧化二铝。由于燃煤成分不同，粉煤灰中三氧化二铝的含量晋中、济南、阳泉地区三氧化二铝含量在31%～38%。 　　根据粉煤灰理化性能的不同，粉煤灰综合利用领域包括：混凝土、砂浆应用；水泥应用；新型墙体材料应用；粉煤灰陶粒应用；粉煤灰提铝等高附加值产??；工程回填用灰等方面。 　　2.粉煤灰综合利用技术现状及进展 　　粉煤灰在材料方面的应用是其最主要的应用途径，也是目前粉煤灰综合利用技术最成熟的方面，在实际应用中具有良好的效果。这里重点介绍粉煤灰在建筑材料方面的应用。 　　2.1生产水泥 　　粉煤灰的化学成分与粘土相似，因此可代替粘土生产水泥，其生产工艺和技术装备与生产普通硅酸盐水泥相同。另外，用粉煤灰作混合材料还可制成粉煤灰水泥，由于其具有较好的耐腐蚀性、抗渗性和干缩性较小等特点，可用于抗裂性、耐腐蚀性要求较高的海事工程、水利工程等。由于粉煤灰中含有一定比例的未燃烧碳，在水泥生产中，通过锻烧熟料可以达到节省燃料的目的。 　　2.2改性混凝土 　　在混凝土中掺入一些粉煤灰，可以改善混凝土性能，尤其是在高性能混凝土中粉煤灰作为功能组分时作用更加明显。用粉煤灰代替部分水泥制成混凝土用在海事工程时，可以防止海水侵蚀，随着粉煤灰含量增加，抗侵蚀能力增强。另外，粉煤灰混凝土后期性能优越，在高层建筑的地下部分、大型设备基础和水工结构中应用较多。粉煤灰可提高混凝土可泵性，C60 混凝土一次泵送高度 350 m的上海东方明珠电视塔就是掺粉煤灰泵送混凝土施工的成功范例。高的水化热会使混凝土内部温度大大超过外部，从而引起较大的温度应力，使混凝土表面产生裂缝，掺粉煤灰可以大大降低混凝土的水化热，如浙江省秦山核电站壁厚 1 m 的混凝土安全壳无裂缝出现