模拟csp工艺制备hi-b钢形变和初次再结晶组织织构的研究-study on deformation and primary recrystallization texture of hi - b steel prepared by simulated csp process.docxVIP

万方数据 万方数据 Abstract Traditional high–temperature-strip-production technology of Hi-B steel reveals considerable drawbacks. Developing cost-effective, energy saving and environmental friendly production methods has become one of the major hotspots among large steel corporations and research institutes. CSP (Compact Strip Production) combines high productivity with excellent strip quality in a perfect way. Thus it is necessary to further develop CSP technology for Hi-B steel production. This article simulated CSP for producing Hi-B steel under experimental conditions, and designed a range of experiments from steelmaking to recrystallization and annealing in laboratory. The major research details were listed below: Hot strip produced with CSP formed obvious organization gradient and texture gradient along thickness. GOSS grains mainly distributed at subsurface near grains with crystal orientation {111} and the number of grains gradually reduced from subsurface to core. The strength of α oriented grains 110//RD gradually increased from surface to core. Moreover, the number of recrystallized grains of normalizing strip also increased. The organization gradient, texture gradient and overall strength of texture of inherited hot-rolled strip reduced. The texture type dramatically changed after cold rolling, which formed incomplete α {001}~{111}110fiber texture and complete γ {111}110~112 fiber texture. When the cold-rolling pressure is above 88%, the strength γ fiber texture reduced and strongly aggregated at {111}110.Meanwhile, the strength of {112}(110) oriented texture significantly reduced. It is more efficient to control cold-rolling pressure below 88% in this experiment. The strength of α fibre texture reduced after first recrystallization which mainly occurred at {118}110. While the strength of γ fiber texture improved and strongly aggregated at {111}112. GOSS texture formed again which mainly concentrated on subsurface of samples. Compared cold-rolled Hi-B steel wit