水溶液中色氨酸还原合成金纳米颗粒的分析及其表征-analysis and characterization of gold nanoparticles synthesized by reduction of tryptophan in aqueous solution.docxVIP

Finally,FTIRanalysesandasimplecontrolexperimentconfirmedthattheindolegroupisthedominatingreducingsegmentinvolvedinthereductionofAu(III).AndpreliminaryexplorationsofmorphologyevolutionfoundthatsnowflakeGNPsexperiencedtheanisotropicgrowthofnucleartothornyparticles,andthenformedbytheiraggregation.While,duetothesurfactantsinduceddirectionalgrowth,GNPsofrod-like,flake(triangular,truncatedtriangularandhexagonal)formed.KEYWORDS：goldnanoparticles,morphology,tryptophan,surfactant,anisotropicgrowth,directionalgrowth目录第一章文献综述..................................................................................................................................11.1金纳米材料的特性及其应用................................................................................................11.1.1金纳米材料的特性.....................................................................................................11.1.2金纳米材料的应用.....................................................................................................31.2金纳米材料的研究现状及制备方法简介...........................................................................51.3不同形貌金纳米颗粒的可控合成........................................................................................71.4色氨酸简介.............................................................................................................................81.5课题来源及研究内容..........................................................................................................10第二章实验及测试方法....................................................................................................................122.1实验试剂与仪器...................................................................................................................122.2色氨酸解离性质...................................................................................................................132.3纳米金颗粒制备的影响因素研究......................................................................................152.3.1不同反应参数下纳米金颗粒的制备............................................