水热法合成yagc荧光粉-hydrothermal synthesis of yagc phosphor.docxVIP

AbstractYAG：Cephosphorhasthemeritofhighchemicalstability,highhardness,highmeltpointandlonglifeetal.Ithasgoodweatherabilityandwillbeverystabilityevenifinthecircumstanceofhumidandultravioletwithoutcoated.ThephosphorandblueLEDchipcanmakeupofopticwhitelight,namelywhiteLED.ThiswhiteLEDhaswideapplicationfutureandwillbecometheforthnewilluminant.ThisarticleusedhydrothermalmethodsynthesizedanaphasephosphormaterialYAG：Ce.Comparedwithconventionalmethodsuchassolid-statereactionsandcombustion,thesamplehavelittlergranularity(diameteris200nm),purerphase,andhavenoconglobation.Comparedwithdifferentreactioncondition,weconcludethatifminglesomeorganicmatterthencannotabilityreducereactionrequirement.Bythestudyofinfluenceofdifferentreactioncircumstancetoproductionsuchassynthesizingtemperature,mingledensityofCe3+,wefindthebestreactioncondition.Thesampleiscubicstructureandhasuniformsize.Theexcitationspectraofsampleisfrom420nmto540nmandemissionspectraisfrom450nmto650nm,sotheemissionlightofsampleandbluelightofLEDshipcanwellmingleopticWightlight.Keywords:hydrothermalsynthesis；YAG:Ce；emissionspectra；excitationspectra目录摘要.................................................................................................................................IABSTRACT.....................................................................................................................II第1章引言..................................................................................................................11.1照明光源的发展历程............................................................................................11.2白光LED技术的实现21.3荧光粉的制备........................................................................................................31.4本论文的研究目的、内容、创新点....................................................................51.4.1研究目的..........................................................................................................51.4.2研究内容....................................................................