浅谈建筑材料中绝热材料.docVIP

浅谈建筑材料中绝热材料 　　摘要：隔热材料应能阻抗室外热量的传入，以及减小室外空气温度波动对内表面温度影响。本文综述了导热系数、导温系数、蓄热系数对材料隔热性能的影响，并且还介绍了建筑上常用保温材料、多孔性保温隔热材料以及其类型的保温隔热材料。 　　关键词：建筑材料；导热系数；保温材料；多孔性保温隔热材料 　　中图分类号：TU761 文献标识码：A文章编号： 　　 　　Abstract: thermal insulation material should be able to impedance outdoor the spreading of the heat, and to decrease the outdoor air temperature fluctuations internal surface temperature influence. This paper reviewed the coefficient of thermal conductivity and temperature conductivity and heat storage coefficient of thermal insulation material influences the performance of, and also introduces the building is used to heat preservation material, porous heat insulating materials and its type of thermal insulation material. 　　Key words: building materials; Coefficient of thermal conductivity; Heat preservation material; Porous thermal insulation material 　　前言：绝热材料和吸声材料都是建筑功能材料的重要品种，他们对建筑物使用功能的质量有重要作用。绝热材料对建筑物的能源消耗有较大影响。在建筑上，将主要作为保温、隔热使用的材料通称为绝热材料。绝热材料通常导热系数值应不大于0.23W/(m?k)，热阻值应不小于4.35(m2?k)/W。 　　1.对材料导热系数的影响 　　 影响材料保温性能的主要因素是导热系数的大小，导热系数越小，保温性能越好。材料的导热系数受以下因素影响：第一个是材料的性质。不同的材料其导热系数是不同的，一般说来，导热系数值以金属最大，非金属次之，液体较小，而气体更小。对于同一种材料，内部结构不同，导热系数也差别较大。一般结晶最大，微晶体结构的次之，玻璃体结构的最小。但对于多孔的绝热材料来说，由于空隙率高，气体对导热系数的影响起着主要作用，而固体部分的结构无论是晶态或玻璃态对其影响都不大；第二是表观密度与孔隙特征。由于材料中固体物质的导热能力比空气要大得多，导热系数较小。在空隙率相同的条件下，空隙尺寸越大，导热系数就越大；互相连通孔隙比封闭孔隙导热性要高。对于表观密度很小的材料，特别使纤维状材料，当其表观密度低于某一极限值时，调动热系数反而会增大，这是由于孔隙增大且互相连通的孔隙大大增多，使对流作用加强，因此这类材料存在一个最佳表观密度，即在这个表观密度时导热系数最小；第三是湿度。材料吸湿受潮后，其导热系数就会增大，这在多空材料中最为明显。 　　2.建筑上常用保温材料 　　2.1 纤维状保温隔热材料 　　2.1.1 石棉及其制品 　　 石棉是一种天然矿物纤维，主要化学成分是含水硅酸镁，具有耐火、耐热、耐酸碱、绝热、防腐、隔音及绝缘等特性。常制成石棉粉、石棉纸板、石棉毡等制品，用于建筑工程的高效能保温及防火覆盖等。 　　2.1.2 矿棉及其制品 　　 矿棉一般包括矿渣棉和岩石棉。矿渣棉所用原料有高炉硬矿渣、铜矿渣等，并加一些调节原料（钙质和硅质原料）。岩棉的主要原料为天然岩石（白云石、花岗岩、玄武岩等）。上述原料经熔融后，用喷吹法或离心法制成细纤维。矿棉具有轻质、不燃、绝热和电绝缘等性能，且原料来源广，成本较低。可制成矿棉板、矿棉毡及管壳等。可用作筑物的墙壁、屋顶、天花板等处地保温和吸声材料，以及热力管道的保温材料。 　　2.1.3 玻璃棉及其制品 　　 玻璃棉是用玻璃原料或碎玻璃经熔融后制成纤维状材料，包括短棉和超细棉两种。 　　2.1.4 植物纤维复合板 　　 以植物纤维为主要才加入胶结料和填料而制成。如木丝板是以木材下脚料制成木丝，加入硅酸溶液及普通硅酸盐水泥混合，经成型、冷压、养护、干燥而制成。甘蔗板是以甘蔗渣为原料，经过蒸制、加压、干燥等工序制成的一种轻质