河南科技学院 2009届本科毕业论文 论文题目: 探讨脉冲电流对H13热模具钢球化退火组织和性能的影响 Discussion on pulse current impact on the spheroidizing organization and performance of the H13 cold molding tool steel 学生姓名：刘铁权 所在院系：机电学院 所学专业：机电技术教育 导师姓名：王焕琴 完成时间：2009 年 5 月15 日 摘 要 H13钢是一种用途广泛的钨系热作模具钢，其含碳量在0.3%左右，属于过共析钢，基本组织为索氏体体和碳化物.H13刚的强度，硬度，耐磨性，和疲劳强度等性能与碳化物的形态，大小以及分布有关，通常H13钢的常规等温退火处理先是保温，然后炉冷再空冷，退火后的组织为球状珠光体和少量的粒状碳化物，可以获得的硬度为210HBS左右，但该处理工艺周期较长，耗能较多，效率低，而且很难在基体上获得粒度小，分布均匀的碳化物，而采用电脉冲球化退火处理后的H13钢效果比较明显，结果表明，新工艺提高了球化速度，球化时间与常规处理的球化时间相比，大大缩短，而且碳化物颗粒细小均匀，球化效果好，硬度适当，比常规退火处理后的硬度低，组织也分布均匀. 关键词：H13钢，球化退火，碳化物，电脉冲处理 Discussion on pulse current impact on the spheroidizing organization and performance of the H13 cold molding tool steel Abstract H13 steel is a widely used line of tungsten hot die steel, the carbon content of about 0.3%, which had eutectoid steel, the basic organization and carbide sorbite just .3 Cr2W8V strength, hardness, wear-resistant sexual, and the fatigue performance and carbides, such as shape, size and distribution, often H13 steel conventional isothermal annealing heat first, and then cold and then air-cooled furnace, annealed for globular organization of granular pearlite and a small amount of carbide, available about 210HBS hardness, but the process cycle is longer, more energy-consuming, inefficient, and very Difficult to obtain in the matrix of small size, carbide distribution, and use of electrical pulses spheroidzing H13 steel treated more obvious effects, results show that the new technology to improve the speed of the ball, the ball time and conventional treatment of the ball time compared to significantly reduce, and even small carbide particles, the ball of effective hardness appropriate than the conventional annealing treatment, the hardness of low distribution organizations. Key words; H13 steel; spheroidizing; carbide; electropulsing. 目 录 TOC \o 1-3 \h \z \u HYPERLINK file:///C:\\Documents%20and%20Settings\\Administrator\\桌面\\12翟小伟毕业论文1.doc \l _Toc200368185#_Toc200368185 1 绪论