粉煤灰和废旧铝铁片在废水处理中应用 　　摘 要：在高温加热、搅拌的条件下，用强酸浸渍粉煤灰和废旧铝、铁片，制得粉煤灰混凝剂，在一定的搅拌条件下，用自制的粉煤灰复合混凝剂处理屠宰废水，在最佳的混凝pH值和最佳混凝剂用量时，处理后的屠宰废水pH值在7左右、COD去除率为92.0%、浊度去除率为92.0%、SS去除率为92.0%、色度去除率为92.0%，充分验证粉煤灰和废旧铝、铁片资源化和在废水处理中应用的可行性。 　　关键词：粉煤灰；铝铁；自制复合混凝剂；废水处理；混凝处理 　　中图分类号：X705文献标识码：B 　　The Application of Fly ash and scrapping aluminum, iron sheets 　　 in slaughter wastewater treatment 　　dijingfen 　　zhaoxian Environmental Monitoring Stationhebeishijiazhuangzhaoxian051530 　　Abstract: In the Conditions of high heat and stirring, using strong acid impregnating fly ash and scrapping aluminum, iron, We can obtain fly ash coagulant, under certain mixing conditions, using the selfmade fly ash composite coagulant treating the slaughterwastewater, with the bestpH and dosage,the pH value of wastewater after treatment is around 7.0, the COD removal rate is 92.0%, the turbidity removal efficiency is 92.0%, and the SS removal rate is 92.0%,the color removal reat is 92.0%, these verify that the fly ash and scraping aluminum, iron can be resourced andapplied in wastewater treatment. 　　Keyword: Fly ash; Aluminum; Iron ;Self-made Composite coagulant;Wastewater treatment; Coagulation treatment 　　1自制复合混凝剂过程及特点 　　在高温加热、搅拌的条件下，用稀盐酸充分浸渍粉煤灰微粒和碎铁、铝片，粉煤灰在酸浸渍后，其表面或微孔内变得更加粗糙，比表面显著增大，这相当于表面被活化，活化后的粉煤灰对有机物的吸附能力更强，同时酸浸粉煤灰提取其中的铁和铝，强酸溶解铁片、铝片形成具有良好混凝效果的铁、铝的高聚物，使得自制粉煤灰混凝剂效果更好。该混凝剂为液体状态，呈淡黄色，用时稀释10倍。经测定该混凝剂各项指标如下： 　　 　　 　　 　　2屠宰废水水质特点 　　实验废水来自一家肉类加工有限公司，该厂废水主要含有屠宰过程中产生的猪血、猪毛、猪粪便、内脏杂物、未消化食物及碎肉、油脂等。废水呈红褐色，溶解性物质含量较高，有机物含量、SS、色度、浊度较高。经测定原水水质指标COD、SS、pH值、浊度、色度如下： 　　 　　 　　 　　3混凝实验 　　3.1混凝水力条件 　　混凝水力条件为：先以250 r/ min快速搅拌2分，再以50 r/ min慢速搅拌15分，沉淀20分。 　　3.2确定混凝剂最小投加量 　　取400ml废水于混凝搅拌机上，以50 r/ min慢速搅拌，加入1ml稀释后混凝剂，稍等几秒再加，直至矾花出现，此剂量即为最小投加量。通过实验，最小投加量为10%的混凝剂4ml。 　　3.3确定混凝的最佳pH值 　　用玻璃杯取8份400ml废水于混凝搅拌机上，调节其pH值分别为4、5、6、7、8、9、10，同步加10%的混凝剂4ml，按照设定混凝水力条件处理废水。混凝后取上清液测定COD、SS、pH值、浊度、色度。测定数据如表3-1： 　　 　　 　　 　　分别作浊度、COD、色度、SS随pH值的变化曲线：由图3-1知pH值在6到7的范围内COD、SS、浊度、色度都达到最小值，所以最佳pH值范围是6到7。 　　 　　 图3-1浊度、COD、色度、SS随pH值的变化曲线