转炉吹炼双渣法造渣技术开发与应用-中国鑛冶工程学会.PDF

轉爐吹煉雙渣法造渣技術開發與應用 Development and application of double slag process in Basic Oxygen Furnace 1 2 3 4 K.L. Chang, Y.Y. Kuo, W.H. Chou, W.J. Hwang The low phosphorus content requirement is essential for production of the high-grade steel. It is great challenge to effectively dephosphorize during BOF (Basic Oxygen Furnace) slagging op eration and to improve production efficiency and cost savings. In this study, we developed a double slag process and applied in the steelmaking operation (1) practices. The lime dissolving mechanism and slagging process were analyzed. The modified processes based on the analy sis result s are successful for production of [P] 50ppm 50ppm low phosphorus steel. Desiliconization slagging and deslagging technology was used in the newborn single blast of Dragon Steel with high silicon hot metal. The benefits of the newly developed process include: (1) rapid slagging reaction (2) improving dephosphorization efficiency during BOF initial blowing period; (2) successfully reducing the amount of waste dumping hot metal; and (3) significant cost savings of BOF operation. 關鍵詞： Key words: Double slag method, low phosphoru s steel, high silicon hot metal 一、前　言