加固淤泥中水泥土机理及的应用 　　摘要：淤泥软弱土层在珠海西区近海地带广泛分布，其物理力学性质极差，承载力低，往往难以满足水利工程建设中对上部结构的承载力和变形要求。为了保证上部结构的安全、正常使用，往往需预先对淤泥进行加固处理，本文通过对珠海西区多个水闸工程的软土地基处理试验，建立了粉喷深层搅拌法用于地基加固的工程质量控制及评定标准，以进一步拓宽深层法在水利工程的应用，探索适应软弱淤泥地层的更合理有效的加固手段。 　　关键词：淤泥;深层搅拌桩;加固机理;地基 　　Abstract: Silt soft soil is widely distributed in the Western District of Zhuhai coastal zone, its physical and mechanical properties of range, low bearing capacity, often difficult to meet the requirement of bearing capacity. In order to ensure the normal use of the safety, the upper structure, often need to silt reinforcement, established the spray powder deep mixing method for quality control and evaluation standards of foundation reinforcement engineering, to further expand the deep application in hydraulic engineering, to explore the soft mud formation more reasonable and effective means of reinforcement. 　　Keywords: silt; deep mixing pile; foundation reinforcement mechanism; 　　中图分类号：P642.13+3文献标识码：A文章编号： 　　 　　粉喷深层搅拌桩是利用水泥作为固化剂的主剂，通过特制的深层搅拌机械在地基深部就地将软弱土和固化剂强制搅拌形成水泥土，利用水泥与软土之间所产生一系列物理、化学作用，使水泥土强度增长提高地基强度。这种方法适用于处理软弱土层，处理后对提高软土地基承载力效果显著，且处理后能很快投入使用。根据近十年来珠海西区水利工程建设中采用粉喷深层搅拌桩对水闸闸基软弱土层的加固工程成果证明，其加固效果良好，经济效益十分明显。 　　 　　1.粉喷深层搅拌桩加固机理 　　（1）水泥的水解、水化：水泥遇水后发生水解与水化，生成氢氧化钙，含水铝酸钙，含水硅酸钙等化合物；其中氢氧化钙和含水铝酸钙溶解于水，随着水解与水化的反应，溶液达到饱和之后，水与水泥继续反应形成凝胶体。 　　（2）离子交换：土颗粒在天然状态下表面带有负电荷，反离子层为阳离子，呈胶体微粒状，反离子层中的Na+，K+能同Ca(OH)2溶液中的Ca2+进行离子交换，使土粒水化膜变薄，土颗粒集合成大的团粒；此外，水泥水化后呈分散状的凝胶颗粒，其比表面积约为原来的1000倍，因而产生很大的表面能，有强烈的吸附活性，能使较大的土团粒进一步结合起来，形成水泥土的团粒结构，并封闭了各土颗粒之间的孔隙，在较为松散的土体内部形成了网络状胶结结构，具有牢固的联结，而宏观上则表现为水泥土的强度大大提高。 　　（3）硬凝反应：水泥水化以后，溶液中析出的大量Ca2+，与Na+、K+进行离子交换，当Ca2+数量超过离子交换的需要量后，则在碱性环境中Ca2+可与土中游离的二氧化硅和三氧化二铝进行化学反应生成不溶于水的稳定结晶化合物，该结晶化合物在空气中和水中逐渐硬化，增大了土体强度，而且由于其结构比较致密，水分不易侵入，从而使水泥土具有足够的水稳定性。 　　（4）碳酸化作用：水泥水化后产生的游离氢氧化钙和空气及水中的二氧化碳通过碳化反应生成不溶于水的碳酸钙，也可以小幅度增加水泥土的强度，只是增长速度较为缓慢。 　　此外，从施工角度来看，水泥搅拌桩中不可避免会存在原状土块和水泥团块，其粒径大小与强制搅拌的程度密切相关；强制搅拌越充分，土块被粉碎得越小，水泥分布到土中越均匀，水泥土结构强度的均一性就越好，即宏观强度也就越高。 　　2. 粉喷深层搅拌桩施工质量控制 　　2.1 施工工艺流程 　　粉喷深层搅拌桩施工工艺流程如下： 　　 　　 　　 　　图1粉喷深层搅拌桩施工工艺流程 　　2.2 施工质量控