铂基多孔石墨烯材料对甲醇电催化氧化的性能研究-材料科学与工程专业论文.docxVIP

内蒙古科技 内蒙古科技大学硕士学位论文 I III Pt/RGO through a different way in which the nano nickel was the reducing agent of the GO, and analyzed the influence of Pt percent on the electrocatalytic performance of Pt/RGO, and at the same time observed the structure of Pt/RGO and the dispersion of Pt nanoparticles. It was got that 13%wt Pt of the Pt/RGO shows higher mass percent activity and poison tolerance than 20%wt Pt and10%wt Pt of Pt/C.With the increase of Pt percent, the electrocatalytic performance shows rise first and fall, the 13wt%Pt of the Pt/RGO shows the best electrocatalytic property among the 7.2wt%、the 13wt% and the 22wt%Pt. Key Words：DMFC；Zn；Nickel；Graphene；Catalyze PAGE PAGE 1 目 录 摘 要 I Abstract II 引 言 1 第一章 文献综述 2 1.1 燃料电池 2 1.1.1 燃料电池概况 2 1.1.2 燃料电池分类 2 1.2 直接甲醇燃料电池（DMFC） 3 1.2.1 直接甲醇燃料电池工作原理 3 1.2.2 直接甲醇燃料电池的发展 4 1.2.3 直接甲醇燃料电池面临的问题与挑战 5 1.3 直接甲醇燃料电池阳极催化剂的研究进展 6 1.3.1 Pt 基电化学催化剂在 DMFC 中应用 7 1.3.2 铂基电化学催化剂的制备方法 7 1.4 碳材料在催化剂载体中的应用 9 1.4.1 石墨烯的制备方法 11 1.4.2 石墨烯三维化 13 1.4.3 石墨烯掺杂 14 1.5 本文选题意义与研究内容 14 第二章 实验材料与研究方法 15 2.1 实验药品与实验仪器 15 2.1.1 实验药品 15 2.1.2 实验仪器及测试设备 15 2.2 样品表征方法 16 2.2.1 扫描电子显微镜分析（SEM） 16 2.2.2 拉曼光谱(Raman) 16 2.2.3 傅里叶红外光谱（FTIR） 16 2.2.4 X 射线光电子能谱仪（XPS） 16 2.2.5 X 射线衍射 17 2.2.6 紫外-可见光分析 (UV-vis) 17 2.2.7 透射电镜 17 2.3 催化剂的电催化性能测试方法 17 第三章 锌还原多孔石墨烯的制备及表征 18 3.1 实验部分 18 3.1.1 氧化石墨烯的制备 18 3.1.2 锌还原氧化石墨烯 18 3.2 结果与讨论 19 3.2.1 红外光谱表征 19 3.2.2 拉曼光谱表征 20 3.2.3 X 射线衍射分析 20 3.2.4 X 射线电子能谱分析 21 3.2.5 热重分析 22 3.2.6 扫描电镜形貌分析 23 3.3 小结 23 第四章 锌还原制备 Pt/RGO 及其对甲醇氧化的催化性能研究 24 4.1 实验部分 24 4.1.1 不同温度锌还原石墨烯载铂 24 4.1.2 不同时间锌还原石墨烯载铂 25 4.1.3 样品铂含量的测定 25 4.1.4 工作电极的制备 25 4.2 结果与讨论 25 4.2.1 铂含量的测定 26 4.2.2 R-Pt/RGO 与商业 Pt/C 催化性能的比较 27 4.2.3 不同还原温度下 Pt/RGO 的电化学催化性能 31 4.2.4 不同还原温度下 Pt/RGO 的电化学催化性能 33 4.3 小结 37 第五章 纳米镍还原氧化石墨烯两步法制备石墨烯载铂 38 5.1 实验部分 38 5.1.1 纳米镍的制备 38 5.1.2 纳米铂的制备 39 5.1.3 纳米 Ni 还原石墨烯载铂 39 5.2 结果与讨论 39 5.2.1 Pt/RGO 与 Pt/C 的催化性能比较 39 5.2.2 不同铂含量 Pt/RGO 的电化学催化性分析 42 5.3 小结 45 结 论 47 参考文献 48 在学研究成果