桥面铺装防水粘结层材料性能的研究.docVIP

桥面铺装防水粘结层材料性能的研究 　　摘要：在不同桥面状态和不同温度条件下，对三种不同的桥面防水粘结层材料进行了剪切实验、拉伸实验和渗水试验室内试验，分析了桥面状态和温度对防水粘结层性能的影响。试验表明，对桥面进行拉毛处理可以提高防水粘结层的强度，且防水粘结层的强度随温度的增加而降低。 　　关键词：防水粘结层 剪切强度 拉拔强度高粘沥青 　　中图分类号： TU535 文献标识码： A 　　 　　Study on The Performance of Waterproof and Cohesive Materials for Bridge Deck Pavement 　　Liu Yun 　　GuanDong HongGao Construction Group Co.,Ltd 　　Abstract：Under different decks and different temperatures, we do shear test, tensile test and laboratory seepage test on the three kinds of bridge deck waterproof and cohesive materials. And we analyze the performance of waterproof and cohesive layer influenced by deck condition and temperature. According to the tests, we can see that it may increase strength of waterproof and cohesive layer by rough coating. And we discover that the strength of waterproof and cohesive layer may decrease with the increase of temperature. 　　Key words：Waterproof and cohesive layer； tensile strength ；shearing strength；high-viscosity asphalt 　　1 前言 　　目前在混凝土桥面沥青混凝土铺装中铺设防水粘结层已经在国内被认可，且通过防水粘结层的使用实践表明，设防水粘结层的桥面铺装具有明显的优势，病害更少，桥梁更耐久。 　　桥面防水是依靠防水材料粘贴到桥面板上，形成具有良好弹性的防水薄膜，隔断水与混凝土的接触，起到防水作用。同时防水材料自身有良好的渗透能力，能从混凝土表面孔隙中进入混凝土内部，堵塞混凝土内部空隙，强化混凝土表面的防水性，提高混凝土的自防水能力。这种双重屏蔽作用保证了防水材料的有效性。 　　本次研究选择了目前混凝土桥面铺装中比较常用的的几种防水粘结层材料(胶粉沥青、SBS沥青和高粘沥青)，在不同的试验条件下进行剪切实验、拉伸实验和渗水试验室内试验，以找出影响防水粘结层的关键因素和合适的防水粘结层材料。 　　2 粘层材料基本性能试验 　　本次试验选用的胶粉沥青是采用中海道路石油沥青A-70掺入20%的40目胎面胶粉；SBS沥青是采用中海道路石油沥青A-70掺入5％韩国LG-4913改性剂。三种防水粘结层材料的基本性能如表1所示。 　　表1 三种防水粘结层材料的基本性质 　　 　　 　　 　　3 防水粘结层剪切试验 　　3.1 试件的制备 　　剪切试验采用C45水泥混凝土，试件尺寸为直径100 mm、高50 mm。到龄期后在混凝土试件上涂不同种类的防水粘结材料 (SBS沥青、胶粉沥青的用量为1.6kg/㎡；高粘沥青的用量为1.2kg/㎡)，按沥青混合料试件成型方法在水泥混凝土试件上加压成型直径100 mm、高63.5 mm的沥青混合料，成型后的试件在室温中静置24 h。 　　3.2 试验结果 　　桥面防水粘结层，包括整个铺装层，是在垂直和水平荷载的综合作用下工作的，因此防水粘结层的抗剪切能力是评价其优劣的重要技术指标之一。夏季高温时，沥青混凝土桥面最高温度在60℃以上。桥面实测表明，高温环境下的剪切力作用对防水粘结层是最不利的。考虑到材料对温度的敏感性，本文进行了不同温度下的抗剪强度测定。为真实模拟混凝土桥面沥青铺装的实际情况，依据模型自行开发大型直剪仪，采用正压力0.7Mpa对组合试件进行直接剪切试验。 　　水泥混凝土的表面特性不同，必然影响防水粘结层的应用效果。本次研究在25℃温度下，试验不同混凝土表面处理对剪切强度的影响，结果如表2所示。 　　 　　表2 水泥混凝土表面不同处理程度时的剪切强