磷酸镁水泥砂浆力学性能实验的研究 　　摘要：磷酸镁水泥作为一种新型的胶凝材料，具有初凝时间早、早期强度高、粘合强度及耐久性好等优点，其工程应用明显增加。然而不同配比对磷酸镁水泥砂浆力学性能有不同影响，本文将分析高温作用后磷酸镁水泥砂浆试件的外观特征及抗压强度变化规律，选择凝结时间较长、抗压强度较高的水泥砂浆试件配比，并在此基础上研究磷酸镁混凝土的相关特性。 　　关键词：磷酸镁；水泥砂浆；高温；力学性能 　　Abstract: the magnesium phosphate cement as a new type of cement materials, with initial setting time early, early high strength, good adhesion strength and durability etc, and its engineering application increased significantly. However different ratio of magnesium phosphate cement mortar mechanical properties have different effects, this article explores the role of high temperature after magnesium phosphate cement mortar specimen appearance characteristics and the compressive strength of the change rule, choose the setting time is longer, compressive strength, high ratio of cement mortar specimens, and based on this study phosphoric acid magnesium concrete related characteristics. 　　Keywords: phosphate magnesium; The cement mortar; High temperature; Mechanical properties 　　 　　 　　中图分类号：TU541文献标识码：A 文章编号： 　　 　　 　　 　　虽然水泥砂浆材料在工程建设中已经得到非常广泛的应用，但当其在高温或局部高温环境中应用时，其性能往往遭到严重的破坏。磷酸镁水泥作为一种新型的胶凝材料，其在常温作用下具有初凝时间早、早期强度高、粘合强度及耐久性好等优点，然而高温作用后的力学性能尚缺乏相关研究。为此作者通过相关实验对水泥砂浆的在高温作用后的抗压强度这一最基本、最重要的一项力学性能进行了实验，得到其相关的规律，为之后磷酸镁混凝土的研究及应用奠定了基础. 　　1 常温下力学性能呢过试验研究 　　1.1试件原材料 　　1. MgO由济南鲁东耐火材料有限公司提供 　　2. 磷酸二氢钾：工业级，含量98%，直接从市场购买。 　　3. 缓凝剂：磷酸盐水泥的缓凝剂有多聚磷酸钠、硼酸及硼砂等，而硼砂是磷酸镁水泥系统中一种最有效的缓凝剂，但其反应机理尚需进一步研究。本实验采用硼砂作为磷酸盐水泥的缓凝剂。硼砂工业级，白色晶体，直接从市场购买。 　　1.2试验仪器与试验过程 　　磷酸镁水泥砂浆实验采用上海新三思计量仪器制造有限公司生产的微机控制电液伺服万能实验机、抗折强度压力机、水泥稠度凝结时间测定仪、水泥胶砂搅拌机等。 　　1. 将水泥胶砂搅拌机砂罐内装入1350g标准砂，根据不同的配比称取相应的氧化镁、磷酸二氢钾、硼砂和水。 　　2. 将大约500g搅拌好的磷酸镁水泥砂浆放入圆模中，然后用砂浆凝结时间测定仪测定其初凝时间，并用秒表记录下从起始时间到初凝所用的时间t（min）。 　　3. 将过程1中搅拌好的大约2000g磷酸镁水泥砂浆倒入钢模中，每个配比制作3条 的磷酸镁水泥砂浆试件。 　　4. 将制作好的水泥砂浆试件置于标准养护室养护。 　　5. 对按照要求养护的试件进行抗折、抗压强度测试，每个配比的试件测试两个，并记录所有实验结果。 　　通过测试不同配比的磷酸镁水泥砂浆试件的凝结时间和抗压强度，挑选出凝结时间大于20分钟及1天抗压强度大于20 MPa的磷酸镁水泥砂浆试件的配比。 　　1.3磷酸镁水泥砂浆凝结时间及抗压强度测定 　　选择以下4个配比制作磷酸镁水泥砂浆试件，尺寸为 ，测定其凝结时间。将磷酸镁水泥砂浆试件置于标准养护条件下养护1天后，测定其抗折、抗压强度。 　　配比1：氧化镁、磷酸二氢钾、