复合材料π接头渐进失效剖析.docVIP

复合材料π接头渐进失效剖析 　　摘要：针对复合材料π接头复杂的失效形式，采用材料刚度退化的方法模拟结构的渐进失效过程.用Abaqus建立某复合材料π接头的三维有限元模型；采用三维Hashin失效准则和Ye分层准则判别复合材料层合板的5种失效形式，将理想弹塑性材料模型应用于胶层材料来模拟胶层材料的失效，在Abaqus中建立考虑复合材料层合板和胶层失效的分析子程序；在子程序中，定义6个场变量代表纤维拉伸破坏、纤维屈曲、基体拉伸开裂、基体压缩开裂、分层失效和胶层失效等6种失效形式.在递增的拉伸载荷作用下对所建模型进行失效分析，结果表明该方法能有效地对复合材料π接头进行初始失效位置及载荷的判别和最终失效预测. 　　关键词：复合材料；π接头；渐进失效分析；Hashin准则；Ye分层准则；胶层失效；Abaqus 　　中图分类号：V214.8；V229；TB115.2 文献标志码： A 　　作者简介： 陈?|艳(1974―)，女，浙江东阳人，讲师，博士，研究方向为航天器结构分析、优化设计、结构优化软件系统开发, 　　 　　(E??mail)chenshenyan@ 　　Progressive failure analysis on composite π joint 　　 　　CHEN Shenyan1, LIN Zhiwei1, MOHAMED Yasser Mahmoud1, 　　HUANG Hai1, LIANG Xianzhu2 　　 　　(1. School of Astronautics, Beijing University of Aeronautics and Astronautics, Beijing 100191, China; 　　2. China Beijing Aeronautical Manufacturing Technology Research Institute, 　　China Aviation Industry Co. I, Beijing 100024, China) 　　 　　Abstract： As to the complex failure modes of composite π joint, the progressive failure procedure of a structure is simulated by material stiffness degradation method. The 3D finite element model of a composite π joint is established by Abaqus; five failure modes of composite laminates are differentiated by using 3D Hashin failure criteria and Ye??delamination criterion, an elastic??perfectly plastic material model is applied to adhesive material to simulate the adhesive failure, and a progressive failure analysis subroutine considering both the composite laminates and adhesive failures is developed in Abaqus, in which six field variables are defined to represent different failure modes: fiber tensile failure, fiber buckling, matrix tensile cracking, matrix compression cracking, delamination failure and adhesive failure. The failure analysis is performed on the model under given increasing tensile loads, and the results show that the method is effective in predicting initial failure position, initial failure load and final failure load for composite π joint. 　　Key words： composite; π joint; progre