钢纤维粉煤灰再生混凝土力学性能的试验研究-结构工程专业论文.docxVIP

II II Abstract The detailed process of recycled aggregate preparation at home and abroad is introduced and evaluated, and according to the production process of recycled aggregate summed up a set of recycled aggregate preparation process in accordance with environmental protection, energy saving and efficient. Analysed of the physical properties of recycled coarse aggregate after the experiments, summed up the root causes that recycled coarse aggregate indicators of the performance is better than natural aggregate were the cement mortar surface parcel of recycled coarse aggregate and accumulation of a large number of microcracks in the composite stress suffered by the preparation process. Application of orthogonal design, scientifically chose the design and orthogonal test scheme of the recycled concrete with steel fiber and fly ash. Then according to the design and orthogonal test scheme preparation,144 pieces of recycled concrete test blocks with steel fiber and fly ash was done,then standard curing period of 28 days. Then the recycled concrete with steel fiber and fly ash components of the cube compressive strength, splitting tensile strength and flexural strength are determined, and analysis the test data by using the numerical analysis method of orthogonal test design.Get the following conclusions: Through the orthogonal analysis can be found that when the replacement of fly ash is within 30%, the quantity of steel fiber in 1.8% the replacement of fly ash is the main factor influencing the compressive strength of the recycled concrete with steel fiber and fly ash, the second is the replacement rate of recycled aggregate, the next is the quantity of steel fiber; steel fiber content is a major factor affecting the splitting tensile and flexural strength of the recycled concrete with steel fiber and fly ash, secondly is the replacement of fly ash, replacement ratio of recycled aggregate. The replacement of fly ash on the 28d cube strength is the same influence to