原位小角X射线散射研究热拉工艺对熔融拉伸法制备的聚丙烯微孔膜结构的影响.docVIP

原位小角X射线散射研宄热拉工艺对熔 融拉伸法制备的聚丙烯微孔膜结构的影 响 王卫徐佳丽林元菲李薛宇孟令蒲李良彬 石河子大学化学化工学院新疆兵团化工绿色过程重 点实验室中国科学技术大学国家同步辐射实验室 采用原位小角X射线散射和扫描电子显微镜研究了热拉过程中，拉伸比和拉伸 温度对熔融拉伸法制备的聚丙烯微孔膜晶体和孔洞结构的影响.研究结果表明， 冷拉、热定型过程中片晶簇被分离开，其内部结构在热拉过程中不发生分离等变 形;随着热拉拉仲比的增加，片晶簇间架桥长度不断增大;与冷拉、热定型样品相 比，热拉后的微孔膜架桥沿垂直于拉伸方向只有较好的周期性.不同的拉伸温度 结果表明，架桥长度随拉伸温度升高而增加;温度过高时架桥会发生熔融. 关键词： 聚丙烯微孔膜;原位小角X射线散射;冷拉-热定型-热拉;微孔;片晶簇; 王卫，男，博士，副教授，主耍从事催化化学及环境学研 宄. :wangwe iww0409@s i na. com 孟令蒲，男，博士，主要从事高性能薄膜拉伸加工物理研 宄. :HYPERLINK mailto:mlp2014@ustc.edu.cnmlp2014@ustc.edu.cn 2017-03-27 基金：W家自然科学基金（批准号 Effect of Hot Stretching on the Structure of Polypropylene Microporous Membranes with in situ Small Angle X-Ray Scattering WANG Wei XU Jiali LIN Yuanfei LI Xueyu MENG Lingpu LI Liangbin School of Chemistry and Chemical Engineering， Key Laboratory for Green Processing of Chemical Engineering of Xinjiang Bingtuan， Shihezi University; National Synchrotron Radiation Laboratory，University of Science and Technology of China; Abstract： With in situ small angle X-ray scattering and scanning electron microscopy measurements, effects of hot stretching temperatures and draw ratios on the lamellae and pore structure of the polypropylene microporous membrane were studied. The results show that the lamellar clusters are separated during the cold stretching and heat setting process, while the internal structures do not undergo separation during the hot stretching process. With the increase of the hot stretching ratio, the bridge length of microporous membrane after hot stretching process increases substantially. Also, it has better periodicity along the equatorial direction compared with the cold-stretching ancl heat-setting samples. The results of different stretching temperatures show that the length of the bridge increases with the increase of the stretching temperature. When the temperature is too high, the bridge will partial ly melt. This work can provide guidance for the structural control during preparation of polypropylene microporous membran