薄片状聚酰亚胺多孔材料研究进展.PDFVIP

薄片状聚酰亚胺多孔材料的研究进展 马晶晶　 　 詹茂盛　 　 王　 凯　 　 刘小艳　 　 吴　 畏 (北京航空航天大学材料科学与工程学院,北京　 100191) 文　 摘　 综述了薄片状聚酰亚胺多孔材料的研究进展,主要介绍了薄片状的聚酰亚胺多孔材料的产品种 类、研究单位、性能指标、应用情况及制备方法,并提出了目前对薄片状聚酰亚胺多孔材料研究存在的问题以及 研究现状,展望了薄片状聚酰亚胺多孔材料在今后的研究方向和发展趋势。 薄片状聚酰亚胺多孔材料,已经作 为垫片用在宇宙飞船的多层隔热系统中,甚至会逐渐替代传统的多层隔热系统材料。 关键词　 聚酰亚胺,薄片,泡沫材料,纤维毡,无纺布 Research Progress of Thin Sheet Polyimide Porous Materials MaJingjing　 　 Zhan Maosheng　 　 Wang Kai　 　 Liu Xiaoyan　 　 Wu Wei (School of Materials Science and Engineering,Beihang University,Beijing　 100191) Abstract　 The recent development of the thin sheet polyimide porous material is reviewed. The product types, properties and applicationofthethinsheetpolyimideporousmaterialareintroducedanditsfutureresearchdirectionas well as the development trends is also pointed out. The thin sheet polyimide porous materials will gradually replace traditional MLI materials as a gasket in the multi-layer insulation system of spacecraft. Key words　 Polyimide,Thin sheet,Foam,Fiber mat,Non-woven fabric 0　 引言 同,薄片状多孔材料厚度范围可以在0.1~5 mm,也 薄片状多孔材料是一种由相互贯通或封闭的孔 称卷材。 薄片状多孔材料由于其厚度优势,质轻、相 洞构成网络结构的平面材料,孔洞的边界或表面由支 对密度低、比强度高、比表面积高、隔音、隔热、渗透性 [1] 柱或平板构成 。 与厚度≤0.1 mm 的薄膜材料不 好等优点。 常见薄片状多孔材料见表1。 表1　 常见薄片状多孔材料 Tab.1　 Thin sheet porous materials 材料 厚度/ mm 性能 原料 生产工艺 3 - 可发性聚苯乙烯、 密度96 kg/ m ,轻柔,耐温 70 ~75℃, 聚苯乙烯泡沫片 1.3~1.5 共混挤出 热导率低 柠檬酸、碳酸氢钠等 聚乙烯管状