养护条件对混凝土毛细吸水性能影响规律的试验研究结构工程专业论文.docxVIP

养护条件对混凝土毛细吸水性能影响规律的试验研究由浇筑面到底面不同位置处的混凝土初始吸水率和同一时刻的累积吸水量逐渐减小，劈 养护条件对混凝土毛细吸水性能影响规律的试验研究 由浇筑面到底面不同位置处的混凝土初始吸水率和同一时刻的累积吸水量逐渐减小，劈 拉强度和超声波速逐渐增大；初始吸水率和孔隙率近似呈线性。 (3)采用改进的混凝土毛细吸水测量装置，避免了传统测重法的人工擦拭和称重 带来的误差，并解决了毛细吸水量无法实时、连续测量的问题。结合通过试验获得的普 通和高强混凝土的初始(S1)和后期吸水率()，基于混凝土毛细吸水的非饱和流体 理论，并采用指数和幂函数两种形式，开展不同养护条件下试件内部水分分布的预测分 析。结果表明，NSC试件内部水分扩散前沿位置随着养护龄期的增长而下降；LWA内 养护混凝土的水分扩散前沿位置在密封养护条件下约为自然养护条件下的0．75倍。另 外，随着平均RCE的提高，试件内部水分扩散前沿的深度不断减小。 关键词：混凝土；养护条件；预湿轻骨料；毛细吸水；相对养护效率；水分扩散前 沿 万方数据 大连理工大学硕士学位论文Experimental 大连理工大学硕士学位论文 Experimental Study on the Influence of Curing Conditions on Capillary Absorption of Concrete Abstract Curing condition of concrete plays a vital role in both the hardening of cemem and the formation of its micro-pore structure．The mechanical property and durability of concrete could be significantly improved by an adequate curing condition．In general，the division of concrete strength grade，the measurement of mechanical property，the evaluation of durability and long-term performance are carried out based on the test results obtained under standard curing condition．However，the curing environment of concrete in practical engineering is quite complicated，which is not only affected by climate and weather conditions，but also restricted by construction technology and operating conditions．Consequently，the performance of concrete measured under standard curing condition could not represent the concrete of practical engineering．As a carrier of migrant corrosive medium，water could cause the expansion／cracking of reinforced concrete structures and the corrosion of reinforcement．Generally，water could penetrate into the interior of the concrete material through the capillary absorption driven by surface tension of pore liquid．Sorptivity has recently been used as all important index for characterizing the concrete durability．It is closely related to the pore structure and its distribution．In order to estimate the effect of curing condition on the performance of concrete，the sorptivity S i