高碳钢盘条轧后冷却过程氧化铁皮生成模拟及工艺优化材料科学与工程专业论文.docxVIP

AbstractA Abstract A layer of iron oxide scale will be formed on the surface of high carbon steel wire rod during the process of cooling after rolling．The oxide scale plays an improtant role in protecting the steel surface during transportion．However,it must be peeled in the subsequent processing．In recent years，due to the advocation of the energy conservation，the improvement of peeling properties of oxide scale is far more important．It is critical to ascertain the factors that affect the stripping properties of the oxide scale and to study the influence of these factors on the peeled properties of the oxide SCale become critical． There are many factors affecting the stripping properties of high carbon steel wire rod，especially the thickness and structure of the oxide scale，which are significantly affected by the cooling technology． Isothermal oxidation test，continuous cooling oxidation test and iron oxide scale peeling test were conducted to study generation laws and the stripping properties of the oxide scale of high carbon steel wire rod during cooling after rolling．Also，the thickness model，structural model and peel performance model of the oxide scale in a lligh carbon steel wire rod were established．The generation process of iron oxide under different conditions and the final stripping properties were simulated based on the equipment and technology conditions in the industrial scenario．In addition，the cooling process corresponding to the best peeling performance of the oxide scale Was obtained under the condition of meeting the requirement of the properties of steels． Keywords：High carbon steel wire；Iron oxide scale；Model；Simulation；Process optimization Ⅱ 万方数据 目 目 录 摘 要 ．．I Abstract． ．． ．． ．． ．． ．． ． ． ．． ．．．． ． ． ． ．． ． ． ．． ．II 第1章绪论 l 1．1研究背景 1 1．2高碳钢线材概况 1 1．2．1国内外线材生产发展现状 ．1 1．2．2线材生产工艺 一3 1．2．3武钢高线车间生产概况 ．5 1．3斯太尔摩冷却控制法 6 1．3．1斯太尔摩冷却控制法的优缺点 ．6 1．3．2武钢的斯太尔摩风冷线设备条件 ．6 1．4氧化铁皮概况 7 1．5金属高温氧化理论 8 1．5．1高温氧化基本过程 ．．8 1．5．2高温氧化热力学 ．．9 1．5．3高温氧化动力学 1 1 1．6